Q160低屈服强度钢高强度螺栓摩擦型连接试验研究
详细信息 本馆镜像全文    |  推荐本文 | | 获取馆网全文
摘要
针对材质为Q160的低屈服强度钢和Q345钢,对表面处理采用喷丸和喷硬质石英砂的试件进行高强度螺栓摩擦型连接试验。通过试验了解两种接触面处理方法对抗滑移系数的影响,并对Q160试件和Q345试件进行比较。试验结果表明,采用硬质石英砂处理试件的抗滑移系数高于采用喷丸处理的试件;Q160试件的摩擦系数并未因为强度降低而降低。因此,提出Q160低屈服强度钢高强度螺栓摩擦型连接设计时可采用与Q345相同的抗滑移系数的建议。
In this paper,the experimental tests of high-strength bolts slip-resistant connection assembled with the plate of both Q160 low yield steel and Q345 low alloy steel were carried out,with treatment methods being shot blast and hard quartz sand blast.The effect of the two treatment methods on slip coefficient was got by the tests,and a comparison between Q160 and Q345 specimens was done.Experimental results showed that the slip coefficient of the specimens with shot blast surface were lower than the ones with hard quartz sand blast surface,the frictional coefficient of Q160 specimen was higher,and it was seemed that the slip coefficient was not reduced due to with the decrease in strength.Therefore,it was suggested that the slip coefficient of Q160 steel plate could be the same value as the Q345 steel plate in the design of high strength bolts slip-resistant connections.
引文
[1]周云,徐彤,俞公骅,等.耗能减震技术研究及应用的新进展[J].地震工程与工程振动,1999,19(2):122-131.
    [2]王华琪,丁洁民,何志军.防屈曲支撑的应用与设计[J].结构工程师,2007,23(4):6-11.
    [3]李国强,孙飞飞,陈素文,等.大吨位国产TJ型屈曲约束支撑的研制与试验研究[J].建筑钢结构进展,2009,11(4):22-26.
    [4]倪志军,刘孝荣,温东辉.建筑抗震用低屈服强度钢厚板的生产与应用[J].工程抗震与加固改造,2009,31(6):129-134.
    [5]温东辉,宋凤明,李自刚.160 MPa级抗震用低屈服强度钢的研究与应用[J].钢铁研究学报,2010,22(1):52-56.
    [6]王玉春,陈鸿德,史永吉,等.高强度螺栓结合[M].北京:中国铁道出版社,1984.
    [7]日本建筑学会.高力ボルト接合設計施工指針[S].1993.
    [8]ANSI/AISC 360-05 Specification for Structural Steel Buildings[S].
    [9]BS EN1993-1-8.Eurocode 3:Design of steel Structures,Part1-8:Design of Joint[S].2005.

版权所有:© 2023 中国地质图书馆 中国地质调查局地学文献中心