再生混凝土吸水率与强度的相关性研究
详细信息    查看全文 | 推荐本文 |
  • 英文篇名:Correlation Between Water Absorption Rate and Strength of Recycled Concrete
  • 作者:纪锋 ; 陈亮亮 ; 张鹏 ; 张红红 ; 孟兆泽 ; 马协刚 ; 任翔
  • 英文作者:JI Feng;CHEN Liang-liang;ZHANG Peng;ZHANG Hong-hong;MENG Zhao-ze;MA Xie-gang;REN Xiang;College of Civil and Hydraulic Engineering,Xinjiang Agricultural University;Chongqing Vocational and Technical College of Water Conservancy and Electric power;
  • 关键词:再生混凝土 ; 粗骨料 ; 吸水率 ; 水胶比 ; 抗压强度 ; 劈拉强度
  • 英文关键词:recycled concrete;;coarse aggregate;;water absorption rate;;water-binder ratio;;compressive strength;;splitting tensile strength
  • 中文刊名:长江科学院院报
  • 英文刊名:Journal of Yangtze River Scientific Research Institute
  • 机构:新疆农业大学水利与土木工程学院;重庆水利电力职业技术学院;
  • 出版日期:2019-03-15
  • 出版单位:长江科学院院报
  • 年:2019
  • 期:03
  • 基金:2016年新疆农业大学研究生科研创新项目(XJAUGRI2016033);2016年新疆农业大学大学生创新项目(2016-XJAUGRI2016033);; 2015年新疆农业大学研究生科研创新项目(dxscx-201610758180);; 新疆水利水电工程重点学科基金项目(xjslgczdxk20101202)
  • 语种:中文;
  • 页:143-148
  • 页数:6
  • CN:42-1171/TV
  • ISSN:1001-5485
  • 分类号:TU528
摘要
为研究再生混凝土吸水率与强度的相关性,选用5~20 mm的再生粗骨料取代天然粗骨料,以再生粗骨料取代率为10%~100%(每10%为一组,共取10组)、3种不同水胶比(0.3,0.4,0.5)的再生混凝土设计试验方案,并选用普通混凝土(取代率0%)作为对照组。在试验组和对照组共同试验的情况下,探讨养护龄期、取代率、水胶比对再生混凝土吸水率与强度的影响规律。结果表明:当取代率保持在≤50%范围内,用再生粗骨料制作的混凝土抗压强度高并且吸水率较低;再生粗骨料取代率在20%附近时,再生混凝土吸水率最低,劈拉强度最高;再生混凝土吸水率和抗压强度这2个检测指标间存在对数关系;再生混凝土和普通混凝土的劈拉强度与吸水率之间也呈幂函数关系。以上结论为检测混凝土强度提供了新的思路和方法,在实际工程中具有重要的指导意义。
        In an attempt to study the correlation between water absorption rate and strength of recycled concrete, we conducted mechanical tests on designed recycled concrete and ordinary concrete as well for comparison. In the preparation of recycled concrete samples, we replaced natural coarse aggregate with recycled coarse aggregate(5-20 mm) in a ratio ranging from 10% to 100% with each ten percent as a test group(in a total of ten groups), and designed the water-binder ratio at three levels(0.3, 0.4, and 0.5). Furthermore we examined the impacts of curing age, coarse aggregate's replacement ratio, and water-binder ratio on the relationship between water absorption rate and strength of recycled concrete. Results unveil that when replacement ratio stays within 0%-50%, the recycled coarse aggregate concrete features with high compressive strength and low water absorption rate; when replacement ratio is about 20%, the water absorption rate reduces to the minimum while the splitting tensile strength reaches the maximum. Moreover, water absorption rate of recycled concrete is in a logarithmic relationship with compressive strength, and a power function relationship with splitting tensile strength for both recycled and ordinary concretes. The conclusions offer new idea and approach for detecting the strength of concrete.
引文
[1] 王立成, 鲍玖文, 李淑红. 损伤混凝土毛细吸水性能试验研究和水分分布预测分析[J]. 大连理工大学学报, 2015, 55(6):597-604.
    [2] 周静海,何海进,孟宪宏,等. 再生混凝土基本力学性能试验[J]. 沈阳建筑大学学报(自然科学版), 2010, 26(3): 464-468.
    [3] 李佳彬, 肖建庄, 黄健. 再生粗骨料取代率对混凝土抗压强度的影响[J]. 建筑材料学报, 2006, 9(3): 297-301.
    [4] 刘宝举, 贺益田, 罗果,等. 养护条件对矿物掺和料混凝土吸水率和电通量的影响[J]. 铁道科学与工程学报, 2015, 12(5): 1058-1063.
    [5] 孙家国,谷艳玲.基于水胶比和再生粗骨料取代率对混凝土性能的影响分析[J].混凝土,2016,(4):64-67.
    [6] 陈亮亮, 吴福飞, 何周勇. 再生混凝土劈拉强度的影响因素及预测模型[J]. 混凝土, 2016, (9): 37-40.
    [7] 崔正龙, 李静. 不同吸水率粗骨料对混凝土强度和干燥收缩性能的影响[J]. 硅酸盐通报, 2016, 35(8): 2396-2399.
    [8] 张保中. 吸水率与混凝土强度关系的初步研究[J]. 科技信息, 2011, (15): 681-732.
    [9] 阎培渝,郑峰. 水泥基材料的水化动力学模型[J]. 硅酸盐学报,2006,34(5):555-559.
    [10] 吴中伟, 廉慧珍. 高性能混凝土[M]. 北京: 中国铁道出版社, 1999.

© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号

地址:北京市海淀区学院路29号 邮编:100083

电话:办公室:(+86 10)66554848;文献借阅、咨询服务、科技查新:66554700