强化硫化铅精矿烧结焙烧技术及机理研究
摘要
硫化铅精矿烧结焙烧是火法炼铅工艺的主要工序之一，铅烧结块质量的好坏将直接影响鼓风炉还原熔炼过程和铅的回收率。
针对目前硫化铅精矿带式烧结机鼓风烧结工艺中所存在的烧结料层透气性差，烧结结块率低、强度差，脱硫效果差等问题，本文以株洲冶炼厂铅精矿为对象，系统研究了硫化铅精矿烧结焙烧的强化技术。
研究表明：通过采用添加剂、强化混合料制粒、热风烧结等技术，以及对烧结机鼓风烧结工艺参数进行优化等措施，可显著改善烧结料层的透气性，强化混合料的烧结焙烧和脱硫，提高烧结结块率和铅烧结块的强度。
当烧结原料配比为返矿65％、圆盘铅10％、浸出渣7％、黄铁矿烧渣4％、石灰石3.8％、宝山铅14％，原料含硫6.0％左右、含铅45.7％左右，并添加0.5％F粘结剂的条件下，进行鼓风烧结焙烧。具体烧结焙烧工艺条件：返矿润湿水分4.0％，混合料水分6.8％，混合时间2min，制粒时间2min，烧结料层高度365mm，烧结鼓风风压4000Pa。在此条件下，可使烧结焙烧脱硫率由60.86％提高到73.73％～76.16％，成品烧结块含硫量由2.15％下降到1.51％～1.64％，ISO转鼓强度由49.93％提高到54.79％～55.44％，烧结利用系数由16.70t／(d·m~2)提高到18.00t／(d·m~2)～20.00t／(d·m~2)的优良结果。
机理研究表明：理想的制粒效果是形成以返矿为核心，以细粒精矿的粘附料的制粒小球结构模型。粘结剂可改善矿粒表面亲水性并在矿粒表面吸附，促进了制粒小球结构模型的形成。提高料层透气性可提高氧气的内扩散速率，而白云石添加剂可提高液相形成温度，延长脱硫时间，提高脱硫反应温度。
物相组成和显微结构分析表明：采取强化措施后，铅烧结块中各物相之间的粘结明显加强，孔隙率减小，结构变得致密，显微强度获得明显改善。烧结块中钙镁橄榄石、镁铁橄榄石等含镁化合物的生成数量增多，游离CaO和SiO_2的数量减少，烧结块自然粉化率降低，质量获得明显改善。
The sintering of lead sulphide concentrate is one of the most important procedures in lead extraction by pyrometallurgy. The qualities of lead sinter present important effects on the reduction smelting and the recovery of lead.
In the paper, focusing on the problems existing the updraught sintering of lead concentrate, such as low bed permeability, low productivity and low qualities of product lead sinter and desulphurization, the enforcing sintering techniques were systematically investigated by using lead concentrate from Zhuzhou metallurgy plant.
It was found that the improvement of permeability of the bed, qualities of lead sinter and desulphurization could be achieved by using additive, strengthening granulating, hot blast firing and adjusting the parameters for sintering.
For a mixed feed of 65% return, 10% mixed lead concentrate, 7% leaching residue, 4% pyrite residue, 3.8% limestone and 14% Baoshan lead concentrate and 0.5% F-additive, the improvement of desulphurization from 60.86% to 73.37%~76.16%, the reduction of sulphur content in product lead sinter from 2.15% to 1.51%~1.64%, the increase of ISO tumbler index from 49.93% to 54.79%~55.44% and production coefficient from 16.70t/(d.m2) to 18.00 t/(d.m2)~20.00 t/(d.m2) were obtained under conditions of 4.0% moisture of return, 6.8% moisture of blend, 2min blend time, 2min granulating time, 365mm height of sinterbed and 4000Pa updraught pressure.
Effective granulation is the formation of granular structure with return as core and concentrate fines as adhering layer. Binders contribute to improvement of surface waterability of returns and fines, and to linkage of fines by adsorbing on surface of fines and returns. High permeability helps to increase oxygen diffusion rate through inner pores, and dolomite acts as additive elevating fluid formation temperature, which results in longer time of desulfurization process. Therefore, desulfurization is enhanced by effective granular structure, high permeability, and dolomite as additive.
Mineralogy composition and microstructure of product lead sinter
were studied. It was shown that the strengthening techniques result in increase in cohesion among components in lead sinter and decrease in porosity as well as improvement of microstructure strength. Furthermore, more compounds containing Mg, such as Ca-Fe olivine and Mg-Fe olivine are formed and free CaO and SiO2 are decreased. Therefore, the degradation index of lead sinter is decreased and the qualities are increased remarkably by the strengthening techniques.
针对目前硫化铅精矿带式烧结机鼓风烧结工艺中所存在的烧结料层透气性差，烧结结块率低、强度差，脱硫效果差等问题，本文以株洲冶炼厂铅精矿为对象，系统研究了硫化铅精矿烧结焙烧的强化技术。
研究表明：通过采用添加剂、强化混合料制粒、热风烧结等技术，以及对烧结机鼓风烧结工艺参数进行优化等措施，可显著改善烧结料层的透气性，强化混合料的烧结焙烧和脱硫，提高烧结结块率和铅烧结块的强度。
当烧结原料配比为返矿65％、圆盘铅10％、浸出渣7％、黄铁矿烧渣4％、石灰石3.8％、宝山铅14％，原料含硫6.0％左右、含铅45.7％左右，并添加0.5％F粘结剂的条件下，进行鼓风烧结焙烧。具体烧结焙烧工艺条件：返矿润湿水分4.0％，混合料水分6.8％，混合时间2min，制粒时间2min，烧结料层高度365mm，烧结鼓风风压4000Pa。在此条件下，可使烧结焙烧脱硫率由60.86％提高到73.73％～76.16％，成品烧结块含硫量由2.15％下降到1.51％～1.64％，ISO转鼓强度由49.93％提高到54.79％～55.44％，烧结利用系数由16.70t／(d·m~2)提高到18.00t／(d·m~2)～20.00t／(d·m~2)的优良结果。
机理研究表明：理想的制粒效果是形成以返矿为核心，以细粒精矿的粘附料的制粒小球结构模型。粘结剂可改善矿粒表面亲水性并在矿粒表面吸附，促进了制粒小球结构模型的形成。提高料层透气性可提高氧气的内扩散速率，而白云石添加剂可提高液相形成温度，延长脱硫时间，提高脱硫反应温度。
物相组成和显微结构分析表明：采取强化措施后，铅烧结块中各物相之间的粘结明显加强，孔隙率减小，结构变得致密，显微强度获得明显改善。烧结块中钙镁橄榄石、镁铁橄榄石等含镁化合物的生成数量增多，游离CaO和SiO_2的数量减少，烧结块自然粉化率降低，质量获得明显改善。
The sintering of lead sulphide concentrate is one of the most important procedures in lead extraction by pyrometallurgy. The qualities of lead sinter present important effects on the reduction smelting and the recovery of lead.
In the paper, focusing on the problems existing the updraught sintering of lead concentrate, such as low bed permeability, low productivity and low qualities of product lead sinter and desulphurization, the enforcing sintering techniques were systematically investigated by using lead concentrate from Zhuzhou metallurgy plant.
It was found that the improvement of permeability of the bed, qualities of lead sinter and desulphurization could be achieved by using additive, strengthening granulating, hot blast firing and adjusting the parameters for sintering.
For a mixed feed of 65% return, 10% mixed lead concentrate, 7% leaching residue, 4% pyrite residue, 3.8% limestone and 14% Baoshan lead concentrate and 0.5% F-additive, the improvement of desulphurization from 60.86% to 73.37%~76.16%, the reduction of sulphur content in product lead sinter from 2.15% to 1.51%~1.64%, the increase of ISO tumbler index from 49.93% to 54.79%~55.44% and production coefficient from 16.70t/(d.m2) to 18.00 t/(d.m2)~20.00 t/(d.m2) were obtained under conditions of 4.0% moisture of return, 6.8% moisture of blend, 2min blend time, 2min granulating time, 365mm height of sinterbed and 4000Pa updraught pressure.
Effective granulation is the formation of granular structure with return as core and concentrate fines as adhering layer. Binders contribute to improvement of surface waterability of returns and fines, and to linkage of fines by adsorbing on surface of fines and returns. High permeability helps to increase oxygen diffusion rate through inner pores, and dolomite acts as additive elevating fluid formation temperature, which results in longer time of desulfurization process. Therefore, desulfurization is enhanced by effective granular structure, high permeability, and dolomite as additive.
Mineralogy composition and microstructure of product lead sinter
were studied. It was shown that the strengthening techniques result in increase in cohesion among components in lead sinter and decrease in porosity as well as improvement of microstructure strength. Furthermore, more compounds containing Mg, such as Ca-Fe olivine and Mg-Fe olivine are formed and free CaO and SiO2 are decreased. Therefore, the degradation index of lead sinter is decreased and the qualities are increased remarkably by the strengthening techniques.
引文
[1] 赵天从．重金属冶金学(下)．北京．冶金工业出版社．1981，第一版：109～184．
[2] 陈国发．重金属冶金学．北京．冶金工业出版社．1992，第一版：79～129．
[3] 彭容秋．有色金属提取冶金手册(锌镉铅铋分册)．北京．冶金工业出版社．1992，第一版：243～422．
[4] 彭容秋．重金属冶金学．中南工业大学出版社．1994，第一版：141～269．
[5] 邱竹贤．有色金属冶金学．北京．冶金工业出版社．1988，第一版．
[6] 马永刚．铅污染现状、原因及对策．中国资源综合利用．2001，No．2：26～28．
[7] 李继强．陈锡永．唐意佳．某冶炼厂环境铅污染及其对人群健康影响的研究，广东卫生防疫．2001，No．1：5～8．
[8] 林淑华．谈炼铁附产品铅的危害及防治．龙岩师专学校．2001，No．3：35～36．
[9] 杨文武，戴永军．金属铅蒸发规律的研究．昆明理工大学学报．1998，No．3：116～120．
[10] 高山．世界铅的消费趋势．世界有色金属．2000，No．3：12～16．
[11] 冯君从．国内外铅锌市场的发展回顾与近期趋势分析．世界有色金属．1999，No．8：29～35．
[12] 陈志宇．对我国目前铅锌工业发展的一点看法．云南冶金．2001，No．6：55～57．
[13] 徐尚春．加强进出口贸易．促进铅工业发展．有色冶炼．2000，No．5：52～55．
[14] 张韬．张殿英．试论我国铅锌工业的发展．湖南有色金属．1996．No．5：38～43．
[15] 冯君从．2002年铅锌市场分析和展望．有色金属(冶炼部分)．2002，No．1：34～38．
[16] 徐传华．铅在现代工业中应用．矿冶．1995，No．3：127～130．
[17] Keith R．Long，John H．Deyong Jr，Steve Ludington．张哲．美国主要金、银、铜、铅、锌矿床．贵金属地质．2002，No．4：241～253．
[18] 陈维平．一种湿法回收废铅蓄电池填料的新技术．湖南大学学报．1996，No．6：111～116
[19] 宋东明．王云坤．铅在非蓄电池领域中的应用．云南冶金．1998增刊：4～9．
[20] 邱定蕃．王成彦．江培海．中国再生有色金属工业的现状及发展趋势．有色金属．2001，No．2：35～38．
[21] 陈家镛．杨守志．柯家骏．湿法冶金的研究和发展．北京．冶金工业出版社．1998，第一版．
[22] 赵天从．湿法炼铅的前景．无污染有色冶金．北京．科学出版社．1992，第一版：64～74．
[23] 赵天从．湿法炼铅试验方案的选择及研究．无污染有色冶金．北京．科学出版社．1992，第一版：75～98．
[24] 周勤俭．陈庭章．杨静等．氧压酸浸处理浮选铜锌铅混和精矿的研究．矿冶工程．1997，No．1：47～50．
[25] 周勤俭．从铜锌铅矿氧压酸浸渣中回收铅和硫的研究．有色金属(冶炼部分)1996，No．4：13～15．
[26] 田秋占．郑安胜．杨光文．三氯化铁浸出硫化铅精矿新工艺．北京科技大学学报．1996，No．1：91～94．
[27] 何海泉．意大利维斯美屯港KSS炼铅技术—kivcet的进展．湖南有色金属．1998，No．1：56～61．
[28] 李炬．李东波．西北铅锌冶炼厂QSL法炼铅工艺的技术改造．有色冶炼．1997，No．3：1～8．
[29] 谭鹏夫．张传福．张瑞瑛．QSL炼铅过程的计算机模拟．中南工业大学学报．1996，No．5：543～546．
[30] 谭鹏夫．张传福．张瑞瑛．QSL炼铅过程的热力学分析．中南工业大学学报．1 996，No．6：666～669．
[31] 杨芝兰．铅鼓风炉熔炼配料最佳化研究．西安建筑科技大学学报．1996，No．1：91～94．
[32] 李仕雄．张传福．童长钿等．提高铅锌烧结结块率的新型高效粘结剂．中国有色金属学报．2000，No．4：569～571．
[33] 李仕雄．刘爱心．李清湘等．有机粘结剂强化铅锌烧结．武汉工业大学学报．1999，No．5：16～18．
[34] 周苹．李支普．汪凤林等．铅鼓风烧结均匀分布的工业性试验．中南工业大学学报．1997，No．1：37～39．
[35] 周建光．王辉．哈萨克斯坦传统法生产铅、锌的近况．有色金属(冶炼部分)．1995，No．2：17～20．
[36] 李贵．铅烧结工艺改造的思路．有色冶炼．2001，No．1：6～9．
[37] 李若贵．株洲冶炼厂铅烧结烟气的治理．有色冶炼．1999，No．4：32～34．
[38] 朱秉彦．魏世发．铅锌烧结机烟气两转两吸制酸装置的设计与方式生产总结．硫酸工业．2001，No．4：20～24．
[39] 周苹．王淑泉．李支普等．改善铅鼓风烧结布风的试验研究与应用．有色冶炼．1995，No．1：34～37．
[40] 郭乐民．硫磺配气法治理铅烧结低浓度SO_2烟气污染的设想．有色冶炼．1999，No．3：41～42．
[41] 张平华．株冶铅烧结高温烟气的治理．有色冶炼．1996，No．3：26～29．
[42] 周苹．李支普．汪凤林．铅鼓风烧结均匀布风的工业性试验．中南工业大学学报．1997，No．1：37～39．
[43] 付一鸣．顾立民．富氧鼓风铅烧结焙烧研究与实践．有色冶炼．1998，No．5：30～33．
[44] 张乐如．铅鼓风烧结技术的研究与实践．湖南有色金属．1999，No．4：18～21．
[45] 陈新民．火法冶金过程物理化学．北京．冶金工业出版社．1981，第一版．
[2] 陈国发．重金属冶金学．北京．冶金工业出版社．1992，第一版：79～129．
[3] 彭容秋．有色金属提取冶金手册(锌镉铅铋分册)．北京．冶金工业出版社．1992，第一版：243～422．
[4] 彭容秋．重金属冶金学．中南工业大学出版社．1994，第一版：141～269．
[5] 邱竹贤．有色金属冶金学．北京．冶金工业出版社．1988，第一版．
[6] 马永刚．铅污染现状、原因及对策．中国资源综合利用．2001，No．2：26～28．
[7] 李继强．陈锡永．唐意佳．某冶炼厂环境铅污染及其对人群健康影响的研究，广东卫生防疫．2001，No．1：5～8．
[8] 林淑华．谈炼铁附产品铅的危害及防治．龙岩师专学校．2001，No．3：35～36．
[9] 杨文武，戴永军．金属铅蒸发规律的研究．昆明理工大学学报．1998，No．3：116～120．
[10] 高山．世界铅的消费趋势．世界有色金属．2000，No．3：12～16．
[11] 冯君从．国内外铅锌市场的发展回顾与近期趋势分析．世界有色金属．1999，No．8：29～35．
[12] 陈志宇．对我国目前铅锌工业发展的一点看法．云南冶金．2001，No．6：55～57．
[13] 徐尚春．加强进出口贸易．促进铅工业发展．有色冶炼．2000，No．5：52～55．
[14] 张韬．张殿英．试论我国铅锌工业的发展．湖南有色金属．1996．No．5：38～43．
[15] 冯君从．2002年铅锌市场分析和展望．有色金属(冶炼部分)．2002，No．1：34～38．
[16] 徐传华．铅在现代工业中应用．矿冶．1995，No．3：127～130．
[17] Keith R．Long，John H．Deyong Jr，Steve Ludington．张哲．美国主要金、银、铜、铅、锌矿床．贵金属地质．2002，No．4：241～253．
[18] 陈维平．一种湿法回收废铅蓄电池填料的新技术．湖南大学学报．1996，No．6：111～116
[19] 宋东明．王云坤．铅在非蓄电池领域中的应用．云南冶金．1998增刊：4～9．
[20] 邱定蕃．王成彦．江培海．中国再生有色金属工业的现状及发展趋势．有色金属．2001，No．2：35～38．
[21] 陈家镛．杨守志．柯家骏．湿法冶金的研究和发展．北京．冶金工业出版社．1998，第一版．
[22] 赵天从．湿法炼铅的前景．无污染有色冶金．北京．科学出版社．1992，第一版：64～74．
[23] 赵天从．湿法炼铅试验方案的选择及研究．无污染有色冶金．北京．科学出版社．1992，第一版：75～98．
[24] 周勤俭．陈庭章．杨静等．氧压酸浸处理浮选铜锌铅混和精矿的研究．矿冶工程．1997，No．1：47～50．
[25] 周勤俭．从铜锌铅矿氧压酸浸渣中回收铅和硫的研究．有色金属(冶炼部分)1996，No．4：13～15．
[26] 田秋占．郑安胜．杨光文．三氯化铁浸出硫化铅精矿新工艺．北京科技大学学报．1996，No．1：91～94．
[27] 何海泉．意大利维斯美屯港KSS炼铅技术—kivcet的进展．湖南有色金属．1998，No．1：56～61．
[28] 李炬．李东波．西北铅锌冶炼厂QSL法炼铅工艺的技术改造．有色冶炼．1997，No．3：1～8．
[29] 谭鹏夫．张传福．张瑞瑛．QSL炼铅过程的计算机模拟．中南工业大学学报．1996，No．5：543～546．
[30] 谭鹏夫．张传福．张瑞瑛．QSL炼铅过程的热力学分析．中南工业大学学报．1 996，No．6：666～669．
[31] 杨芝兰．铅鼓风炉熔炼配料最佳化研究．西安建筑科技大学学报．1996，No．1：91～94．
[32] 李仕雄．张传福．童长钿等．提高铅锌烧结结块率的新型高效粘结剂．中国有色金属学报．2000，No．4：569～571．
[33] 李仕雄．刘爱心．李清湘等．有机粘结剂强化铅锌烧结．武汉工业大学学报．1999，No．5：16～18．
[34] 周苹．李支普．汪凤林等．铅鼓风烧结均匀分布的工业性试验．中南工业大学学报．1997，No．1：37～39．
[35] 周建光．王辉．哈萨克斯坦传统法生产铅、锌的近况．有色金属(冶炼部分)．1995，No．2：17～20．
[36] 李贵．铅烧结工艺改造的思路．有色冶炼．2001，No．1：6～9．
[37] 李若贵．株洲冶炼厂铅烧结烟气的治理．有色冶炼．1999，No．4：32～34．
[38] 朱秉彦．魏世发．铅锌烧结机烟气两转两吸制酸装置的设计与方式生产总结．硫酸工业．2001，No．4：20～24．
[39] 周苹．王淑泉．李支普等．改善铅鼓风烧结布风的试验研究与应用．有色冶炼．1995，No．1：34～37．
[40] 郭乐民．硫磺配气法治理铅烧结低浓度SO_2烟气污染的设想．有色冶炼．1999，No．3：41～42．
[41] 张平华．株冶铅烧结高温烟气的治理．有色冶炼．1996，No．3：26～29．
[42] 周苹．李支普．汪凤林．铅鼓风烧结均匀布风的工业性试验．中南工业大学学报．1997，No．1：37～39．
[43] 付一鸣．顾立民．富氧鼓风铅烧结焙烧研究与实践．有色冶炼．1998，No．5：30～33．
[44] 张乐如．铅鼓风烧结技术的研究与实践．湖南有色金属．1999，No．4：18～21．
[45] 陈新民．火法冶金过程物理化学．北京．冶金工业出版社．1981，第一版．
© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号 地址：北京市海淀区学院路29号 邮编：100083 电话：办公室：(+86 10)66554848；文献借阅、咨询服务、科技查新：66554700 |