在某新型弹药中,双蔗醛(SZQu)推进剂与丁腈橡胶共存。为了探究SZQu推进剂与丁腈橡胶的相互作用,以及丁腈橡胶密封圈的安全寿命,对在75℃条件下分别老化了7d、20d、35d和50d的样品进行了检测。研究结果表明:在储存过程中丁腈橡胶对SZQu推进剂的安全性能影响不大,两者之间的外相容性较好;混合体系中丁腈橡胶的拉断伸长率在老化20d后变为95%,在75℃老化条件下,混合体系中丁腈橡胶密封圈的安全寿命达到20d。
In a certain new type of ammunition,SZQu propellant and NBR is in a sealed system.in order to research the exterior compatibility between SZQu propellant and NBR,and the safe life of NBR,the sample which was aged for 7,20,35 and 50 dunder the condition of 75℃ was tested,respectively.The results showed that NBR had a limited influence on SZQu propellant in the ageing process,the exterior compatibility between SZQu propellant and NBR was good.the elongation at break of NBR in the mixed system was 95% after aging for 20 d.the life of NBR was 20 days,which was aged under the condition of 75℃ in the mixed system.
引文
[1]何玉财,许建和.腈水解酶在羧酸合成中的研究进展[J].生物加工过程,2009,7(1):7-12.
[2]吴中柳,李祖义.氰基水解酶在有机合成中的应用[J].有机化学,2001,21(1):25-32.
[3]赵凤起,王新华.双基推进剂装药包覆层间硝化甘油迁移及抑制[J].固体火箭技术,1993(2):69-74.
[4]邵自强,Yu M L.HYCAR组成对它与NC相容性的影响[J].火炸药学报,2010(2):26-28.
[5]刘继华.火药物理化学性能[M].北京:北京理工大学出版社,1997,12-89.
[6]李咏今.丁腈橡胶烘箱加速老化与室内自然老化相关性的研究[J].特种橡胶制品,2001,22(4):51-56.
[7]张发源.3种丁腈橡胶硫化胶加速老化与室内自然老化压缩应力松弛变化[J].特种橡胶制品,2001,22(4):35-40.
[8]周吉玉,李贵贤,范宗良.丁腈橡胶的热老化性能[J].石油化工应用,2009,28(2):82-85.
[9]肖鑫,赵云峰,许文,等.橡胶材料加速老化实验及寿命评估模型的研究进展[J].宇航材料工艺,2007(1):5-10.
[10]左玉芬,罗雪梅,周建华.温湿度作用下炸药与相关物的相容性研究[J].含能材料,2000,8(4):171-174.
[11]左玉芬,常昆,韦力元,等.炸药和高分子材料在老化过程中的相容性[M].北京:中国工程物理研究院,2002,347-348.
[12]李昂.橡胶的老化现象及其老化机理[J].特种橡胶制品,2009,30(5):56-67.
[13]楚士晋.炸药热分析[M].北京:科学出版社,1994,23-189.
[14]韩光烈,黎留鑫,赵长友,等.硝化甘油生产安全技术与管理[M].北京:国防工业出版社,1988,12-93.
[15]丛川波,邹功文,孟晓宇,等.氢化丁腈橡胶在高温盐酸中的老化过程[J].高分子材料科学与工程,2016,32(3):118-123.