摘要
以聚乙烯高分子添加不同含量石墨烯双螺杆挤出制备的复合材料为基材,利用单螺杆精密线材生产线制备了基于熔融沉积成型(FDM)的3D打印样条。通过XRD和SEM对复合材料力学性能、导电性能、导热性能进行了测试表征,得到了样品的屈服应力点以及不同石墨烯含量下样品的导电、导热规律。结果表明,用该方法制备的纳米复合材料粒径分布均匀,其3D打印线材可用于聚乙烯基石墨烯复合多孔球形阻隔防爆材料3D打印。
The 3D printing wire based on fused deposition modeling(FDM) were successfully prepared by single-screw extruder, whose raw materials were made by using polyethylene based composites filled with different graphene content by twin-screw extruder. The mechanical properties, electrical conductivity and thermal conductivity of the composites were characterized by XRD and SEM. The yield stress point and the conductivity and thermal conductivity of the composites with different graphene content were obtained. The results show that the particle size distribution of the nanocomposites prepared by this method is uniform, and the wire of polyethylene-based composites filled with graphene can be used for 3D prin-ting of porous spherical barrier and explosion-proof materials.
引文
1周醒,夏元梦,蔺海兰,等.复合材料学报,2017,34(4),699.
2郝艳萍.氧化石墨烯/聚合物复合材料的制备与性能.硕士学位论文,东华大学,2017.
3赵晓凤.石墨烯/PET复合材料的制备及性能研究.硕士学位论文,浙江理工大学,2017.
4于方波.石墨烯与聚烯烃的复合方法及其对聚烯烃改性效果的研究.硕士学位论文,华侨大学,2016.
5邓艳丽.苯乙烯系聚合物导电复合材料的制备与性能研究.硕士学位论文,安徽大学,2017.
6张浪浪,刘祥萱,王煊军.火炸药学报,2017,40(5),88.
7张有智,李正莉,王煊军,等.化学推进剂与高分子材料,2008,6(3),20.
8周春波,王煊军,慕晓刚.化学推进剂与高分子材料,2017,15(5),86.
9杨真理,鲁长波,周友杰,等.安全与环境工程,2016,23(2),130.
10邢志祥,张成燕.工业安全与环保,2013,39(12),30.
11高建村,庞磊,孟倩倩.中国安全科学学报,2013,23(8),43.
12邓祥义,胡海平.化工进展,2002,21(10),261.
13喻慧文,徐百平,庄文柳,等.工程塑料应用,2017,45(1),7.
14耿孝正.中国塑料,2005(2),31.
15吴京,殷敬华.塑料,2003,32(1),42.
16肖建华.塑料工业,2016,44(6),46.
17 Cheng S,Chen X,Huan Y G,et al.Macromolecules,2011,45(2),993.
18周友杰,鲁长波,熊春华,等.化学推进剂与高分子材料,2016,14(2),46.
19邢志祥,杜贞,欧红香,等.安全与环境工程,2015,22(2),112.
20 Lei Z,Xie L F,Han Z W.Fire Science&Technology,2014,50(4),477.