摘要
采用无皂乳液聚合法制备以正十八烷和硬脂酸丁酯复合相变材料为芯材、聚甲基丙烯酸甲酯为壁材的相变纳米胶囊.分别引入季戊四醇三丙烯酸酯(PETA)和N,N′-亚甲基双丙烯酰胺(BIS)对壁材聚合物进行交联改性,透射电镜(TEM)结果表明,PETA交联的纳米胶囊形貌更为规整,分散性和成囊性较好.然后,用示差扫描量热仪(DSC)和热重分析仪(TGA)对PETA交联的纳米胶囊和未交联的纳米胶囊进行储热性能和耐热性能分析表明,交联剂的引入增大了复合相变材料和壁材聚合物的起始失重温度,稳定性得到提高,且交联剂赋予聚合物的致密交联网络阻缓了芯材的逸出,相变焓升高.
Nanoencapsulated phase change materials with n-octadecane and n-butyl stearate as binary cores and crosslinked poly(methyl methacrylate)as shell were prepared through surfactant-free emulsion polymerization.Pentaerythritol triacrylate(PETA)and N,N′-methylene bisacrylamide(BIS)were used as crosslinking agents to modify the shell polymer,respectively.The results of transmission electron microscopy(TEM)showed that the morphology of nanocapsules with PETA as crosslinking agent was more regular and had better dispersive and cystic properties,compared with BIS as crosslinking agent.Then,the thermal storage and heat resistance properties of PETA crosslinked nanocapsules and uncrosslinked nanocapsules were analyzed by differential scanning calorimeter(DSC)and thermogravimetric analyzer(TGA),showing that the introduction of crosslinking agent can effectively improve the stability of nanocapsules based on the increase of initial weight loss temperature of the binary phase change materials and shell polymer,and the dense crosslinking network endowed by crosslinking agent can slow down the escape of core material and thus increase the phase change enthalpy.
Nanoencapsulated phase change materials with n-octadecane and n-butyl stearate as binary cores and crosslinked poly(methyl methacrylate)as shell were prepared through surfactant-free emulsion polymerization.Pentaerythritol triacrylate(PETA)and N,N′-methylene bisacrylamide(BIS)were used as crosslinking agents to modify the shell polymer,respectively.The results of transmission electron microscopy(TEM)showed that the morphology of nanocapsules with PETA as crosslinking agent was more regular and had better dispersive and cystic properties,compared with BIS as crosslinking agent.Then,the thermal storage and heat resistance properties of PETA crosslinked nanocapsules and uncrosslinked nanocapsules were analyzed by differential scanning calorimeter(DSC)and thermogravimetric analyzer(TGA),showing that the introduction of crosslinking agent can effectively improve the stability of nanocapsules based on the increase of initial weight loss temperature of the binary phase change materials and shell polymer,and the dense crosslinking network endowed by crosslinking agent can slow down the escape of core material and thus increase the phase change enthalpy.
引文
[1]Wang T,Wang S,Luo R,et al.Microencapsulation of phase change materials with binary cores and calcium carbonate shell for thermal energy storage[J].Applied Energy,2016,171:113-119.
[2]Jiang F,Wang X,Wu D.Design and synthesis of magnetic microcapsules based on n-eicosane core and Fe3O4/SiO2hybrid shell for dual-functional phase change materials[J].Applied Energy,2014,134:456-468.
[3]Li J,Liu H,Wang X,et al.Development of thermoregulatory enzyme carriers based on microencapsulated N-docosane phase change material for biocatalytic enhancement of amylases[J].ACS Sustainable Chemistry&Engineering,2017,9(5):8 396-8 406.
[4]Chen Z,Wang J,Yu F,et al.Preparation and properties of graphene oxide-modified poly(melamine-formaldehyde)microcapsules containing phase change material n-dodecanol for thermal energy storage[J].Journal of Materials Chemistry A,2015,21(3):11 624-11 630.
[5]丘晓琳,唐国翌,宋国林,等.交联聚甲基丙烯酸月桂酯/正十八烷相变微胶囊的制备与性能研究[J].化工新型材料,2016,44(2):55-57.
[6]顾相伶,朱晓丽,孔祥正.等.乙醇或乙醇-水为新的溶剂体系沉淀聚合制备单分散聚合物微球[J].化学学报,2009,67(21):2 486-2 494.
[7]刘欢,魏忠.聚甲基丙烯酸丁酯纳米粒子乳液的制备工艺[J].石河子大学学报(自然科学版),2013,31(3):382-386.
[8]丘晓琳.丙烯酸树脂基相变储能微胶囊的制备与性能研究[D].北京:清华大学,2013.
[2]Jiang F,Wang X,Wu D.Design and synthesis of magnetic microcapsules based on n-eicosane core and Fe3O4/SiO2hybrid shell for dual-functional phase change materials[J].Applied Energy,2014,134:456-468.
[3]Li J,Liu H,Wang X,et al.Development of thermoregulatory enzyme carriers based on microencapsulated N-docosane phase change material for biocatalytic enhancement of amylases[J].ACS Sustainable Chemistry&Engineering,2017,9(5):8 396-8 406.
[4]Chen Z,Wang J,Yu F,et al.Preparation and properties of graphene oxide-modified poly(melamine-formaldehyde)microcapsules containing phase change material n-dodecanol for thermal energy storage[J].Journal of Materials Chemistry A,2015,21(3):11 624-11 630.
[5]丘晓琳,唐国翌,宋国林,等.交联聚甲基丙烯酸月桂酯/正十八烷相变微胶囊的制备与性能研究[J].化工新型材料,2016,44(2):55-57.
[6]顾相伶,朱晓丽,孔祥正.等.乙醇或乙醇-水为新的溶剂体系沉淀聚合制备单分散聚合物微球[J].化学学报,2009,67(21):2 486-2 494.
[7]刘欢,魏忠.聚甲基丙烯酸丁酯纳米粒子乳液的制备工艺[J].石河子大学学报(自然科学版),2013,31(3):382-386.
[8]丘晓琳.丙烯酸树脂基相变储能微胶囊的制备与性能研究[D].北京:清华大学,2013.