摘要
近年纳米TiO_2光催化技术在生态道路中的应用备受关注。因路面材质的不同,纳米TiO_2光催化路面材料的制备方法也有所差异,影响该材料尾气降解效率的主要因素包括纳米TiO_2的掺量、污染物浓度、光源与光照强度等。目前纳米TiO_2光催化技术在水泥混凝土路面、沥青路面和道路附属设施中已得到了应用,但还存在光催化效率不足、在沥青基的负载技术研究不足等诸多问题,有待进一步的深入研究开发。
The research progress of nano TiO_2 photocatalysis technology applied in ecological road was described.Firstly,the general preparing methods of nano TiO_2 photocatalytic pavement material and the influence factors of degradation efficiency were summarized.Then the application status of nano TiO_2 photocatalytic technology in ecological road,including the application in cement concrete pavement,asphalt pavement and ancillary facilities of roads,were discussed in detail.Its existing shortcomings and problems as well as the corresponding improvement measures were put forward.Finally,the application of material in the ecological road in the future was prospected.
The research progress of nano TiO_2 photocatalysis technology applied in ecological road was described.Firstly,the general preparing methods of nano TiO_2 photocatalytic pavement material and the influence factors of degradation efficiency were summarized.Then the application status of nano TiO_2 photocatalytic technology in ecological road,including the application in cement concrete pavement,asphalt pavement and ancillary facilities of roads,were discussed in detail.Its existing shortcomings and problems as well as the corresponding improvement measures were put forward.Finally,the application of material in the ecological road in the future was prospected.
引文
[1]张忠金,关磊.汽车尾气净化催化剂及载体的研究进展[J].化工新型材料,2015,43(4):21-23.
[2] Fujishima A,Honda K.Electrochemical photocatalysis of water at a semiconductor electrode[J].Nature,1972,238(5358):37-38.
[3]贾劲松,赵根成,王朝明,等.溶胶-凝胶法制备纳米TiO2光催化剂的应用研究进展[J].四川化工,2013,16(3):20-24.
[4]李凡修,陆晓华,梅平.微波法制备纳米TiO2材料的研究进展[J].材料导报,2007,21(f11):61-64.
[5]韦庆婷,郭莉,王丹军,等.纳米TiO2的溶胶-微波法合成及其光催化性能研究[J].环境科学与技术,2009,32(3):1-4.
[6]薛寒松,顾铭,曾强,等.微波水热合成法制备TiO2纳米管的晶型和形貌研究[J].化工新型材料,2015,43(11):182-184.
[7]叶青,莫荣辉,余亚超,等.掺氮改性纳米TiO2光催化材料的聚合物水泥砂浆的应用研究[J].新型建筑材料,2009,36(4):15-17.
[8]关强,陈萌.公路水泥混凝土路面喷涂纳米TiO2净化机动车排放污染物研究[J].公路交通科技,2009,3(26):154-158.
[9]徐世法,苑广友,许鹰,等.水基TiO2涂覆液降解汽车尾气效果评价研究[J].北京建筑大学学报,2016,32(1):27-30.
[10]刘成虎,连瑞扬,任冶.纳米TiO2光催化技术在沥青路面中的应用研究[J].交通运输研究,2015,1(5):75-81.
[11]匡亚川,张召环,季小勇,等.具有降解汽车尾气性能的纳米TiO2光催化水泥浆体研究[J].功能材料,2017,48(2):2241-2246.
[12]都雪静,许洪国,关强,等.纳米TiO2含量对汽车尾气因子降解效能影响试验研究[J].公路交通科技,2007,24(10):155-158.
[13]石惠.纳米TiO2光催化净化汽车尾气中NOx的效率分析[D].黑龙江:东北林业大学,2009.
[14]雷雨滋.降解汽车尾气与缓减城市热岛效应的沥青混合料研究[D].陕西:长安大学,2014.
[15]谭忆秋,李洛克,魏鹏,等.可降解汽车尾气材料在沥青路面中的应用性能评价[J].中国公路学报,2010,23(6):21-27.
[16]乔晓军,李佩,文龙.纳米二氧化钛环保涂料降解汽车尾气氮氧化合物效果研究[J].施工技术,2014,43(S):664-666.
[17]钱春香,赵联芳,付大放,等.温湿度和光强对水泥基材料负载纳米TiO2光催化氧化氮氧化物的影响[J].环境科学学报,2005,25(5):623-630.
[18]田地,张彭义,余刚.挥发性有机物光催化降解研究进展[J].上海环境科学,2000,19(4):162-166.
[19] Avlla P.Gas-phase photo-assi sted mineralization of monolithic Ti tanium catalysts[J].Application of Catalyst B:Environ,1998,17:75-88.
[20] Asadi S,Hassan M,Nadiri A.Artificial intelligence modeling to evaluate field performance of photocatalytic asphalt pavement for ambient air purification[J].Environmental Science and Pollution Research,2014,21(14):8847-8857.
[21]张可喜.日本二氧化钛光催化剂技术的应用现状和前景[N].新华社东京,1999.
[22]李丽,钱春香.南京长江三桥光催化功能性混凝土路去除汽车排放氮氧化物的研究[J].河南科技大学学报(自然科学版),2009,30(1):49-52,68.
[23] Anne Beeldens.“第8届国际混凝土路面砖”论文精选利用环保型混凝土路面砖净化安特卫普市城区的空气[J].建筑砌块与砌块建筑,2008(3):30-32,34.
[24]劳拉.冈萨雷斯.Miqueo.带空气净化功能的新型混凝土路面砖[J].建筑砌块与砌块建筑,2014(2):30-31.
[25]马永财,于建国.光催化降解汽车尾气路面喷洒机的研究[J].森林工程,2009,25(4):53-54.
[26]徐海铭,刘黎萍,孙立军,等.纳米二氧化钛在实际道路工程中的应用[J].公路工程,2011,36(4):189-192,198.
[27] Osborn D,Hassan M,Asadi S,et al.Durability quantification of TiO2surface coating on concrete and asphalt pavements[J].Journal of Materials in Civil Engineering,2014,26(2):331-337.
[28]谢函.安吉有条能“吃”尾气的公路[J].中国公路,2017(2):90-91.
[29]杜晨薇.这条路上,汽车尾气边排边降解[N].解放日报,2017-06-11(001).
[30]李思童,李书飞,王超,等.纳米二氧化钛雾封层技术及其在工程中的应用[J].城市道桥与防洪,2018(2):44-47,61.
[31]孙立军,徐海铭,李剑飞,等.纳米二氧化钛处治汽车尾气效果与应用方法的研究[J].公路交通科技,2011,28(4):153-158.
[32]刘小强,杜仕国,闫军,等.纳米二氧化钛改性及其在涂料中的应用[J].化工时刊,2004,18(11):13-16.
[33]姚文静.欧盟研发新一代建筑用二氧化钛材料[J].中国钛业,2017(1):52.
[34]高伟,吴凤清,罗臻,等.TiO2晶形与光催化活性关系的研究[J].高等学校化学学报,2001,22(4):660-662.
[35] Choi W,Termin A,Hoffmann M R.The role of metal ion dopants in quantum-sized TiO2:correlation between photoreactivity and charge carried recombination dynamics[J].J Phys Chem,1994,98(5):13669-13679.
[36] Asahi R,Morikawa T,Ohwaki T,et al.Visible-Light photocatalysis in nitrogen-doped titanium oxides[J].Science,2001,20(3):301-307.
[37]王振领,李敏,刘天学,等.TiO2膜的光敏化及灭菌活性研究[J].陕西师范大学学报(自然科学版),2002,3(30):87-89.
[38] Spanhel L,Weller H,Henglein A.Photochemistry of semiconductor colloids electron injection from illuminated CdS into attached TiO2and ZnO particles[J].J Am Chem Soc,1987,109:6632-6635.
[2] Fujishima A,Honda K.Electrochemical photocatalysis of water at a semiconductor electrode[J].Nature,1972,238(5358):37-38.
[3]贾劲松,赵根成,王朝明,等.溶胶-凝胶法制备纳米TiO2光催化剂的应用研究进展[J].四川化工,2013,16(3):20-24.
[4]李凡修,陆晓华,梅平.微波法制备纳米TiO2材料的研究进展[J].材料导报,2007,21(f11):61-64.
[5]韦庆婷,郭莉,王丹军,等.纳米TiO2的溶胶-微波法合成及其光催化性能研究[J].环境科学与技术,2009,32(3):1-4.
[6]薛寒松,顾铭,曾强,等.微波水热合成法制备TiO2纳米管的晶型和形貌研究[J].化工新型材料,2015,43(11):182-184.
[7]叶青,莫荣辉,余亚超,等.掺氮改性纳米TiO2光催化材料的聚合物水泥砂浆的应用研究[J].新型建筑材料,2009,36(4):15-17.
[8]关强,陈萌.公路水泥混凝土路面喷涂纳米TiO2净化机动车排放污染物研究[J].公路交通科技,2009,3(26):154-158.
[9]徐世法,苑广友,许鹰,等.水基TiO2涂覆液降解汽车尾气效果评价研究[J].北京建筑大学学报,2016,32(1):27-30.
[10]刘成虎,连瑞扬,任冶.纳米TiO2光催化技术在沥青路面中的应用研究[J].交通运输研究,2015,1(5):75-81.
[11]匡亚川,张召环,季小勇,等.具有降解汽车尾气性能的纳米TiO2光催化水泥浆体研究[J].功能材料,2017,48(2):2241-2246.
[12]都雪静,许洪国,关强,等.纳米TiO2含量对汽车尾气因子降解效能影响试验研究[J].公路交通科技,2007,24(10):155-158.
[13]石惠.纳米TiO2光催化净化汽车尾气中NOx的效率分析[D].黑龙江:东北林业大学,2009.
[14]雷雨滋.降解汽车尾气与缓减城市热岛效应的沥青混合料研究[D].陕西:长安大学,2014.
[15]谭忆秋,李洛克,魏鹏,等.可降解汽车尾气材料在沥青路面中的应用性能评价[J].中国公路学报,2010,23(6):21-27.
[16]乔晓军,李佩,文龙.纳米二氧化钛环保涂料降解汽车尾气氮氧化合物效果研究[J].施工技术,2014,43(S):664-666.
[17]钱春香,赵联芳,付大放,等.温湿度和光强对水泥基材料负载纳米TiO2光催化氧化氮氧化物的影响[J].环境科学学报,2005,25(5):623-630.
[18]田地,张彭义,余刚.挥发性有机物光催化降解研究进展[J].上海环境科学,2000,19(4):162-166.
[19] Avlla P.Gas-phase photo-assi sted mineralization of monolithic Ti tanium catalysts[J].Application of Catalyst B:Environ,1998,17:75-88.
[20] Asadi S,Hassan M,Nadiri A.Artificial intelligence modeling to evaluate field performance of photocatalytic asphalt pavement for ambient air purification[J].Environmental Science and Pollution Research,2014,21(14):8847-8857.
[21]张可喜.日本二氧化钛光催化剂技术的应用现状和前景[N].新华社东京,1999.
[22]李丽,钱春香.南京长江三桥光催化功能性混凝土路去除汽车排放氮氧化物的研究[J].河南科技大学学报(自然科学版),2009,30(1):49-52,68.
[23] Anne Beeldens.“第8届国际混凝土路面砖”论文精选利用环保型混凝土路面砖净化安特卫普市城区的空气[J].建筑砌块与砌块建筑,2008(3):30-32,34.
[24]劳拉.冈萨雷斯.Miqueo.带空气净化功能的新型混凝土路面砖[J].建筑砌块与砌块建筑,2014(2):30-31.
[25]马永财,于建国.光催化降解汽车尾气路面喷洒机的研究[J].森林工程,2009,25(4):53-54.
[26]徐海铭,刘黎萍,孙立军,等.纳米二氧化钛在实际道路工程中的应用[J].公路工程,2011,36(4):189-192,198.
[27] Osborn D,Hassan M,Asadi S,et al.Durability quantification of TiO2surface coating on concrete and asphalt pavements[J].Journal of Materials in Civil Engineering,2014,26(2):331-337.
[28]谢函.安吉有条能“吃”尾气的公路[J].中国公路,2017(2):90-91.
[29]杜晨薇.这条路上,汽车尾气边排边降解[N].解放日报,2017-06-11(001).
[30]李思童,李书飞,王超,等.纳米二氧化钛雾封层技术及其在工程中的应用[J].城市道桥与防洪,2018(2):44-47,61.
[31]孙立军,徐海铭,李剑飞,等.纳米二氧化钛处治汽车尾气效果与应用方法的研究[J].公路交通科技,2011,28(4):153-158.
[32]刘小强,杜仕国,闫军,等.纳米二氧化钛改性及其在涂料中的应用[J].化工时刊,2004,18(11):13-16.
[33]姚文静.欧盟研发新一代建筑用二氧化钛材料[J].中国钛业,2017(1):52.
[34]高伟,吴凤清,罗臻,等.TiO2晶形与光催化活性关系的研究[J].高等学校化学学报,2001,22(4):660-662.
[35] Choi W,Termin A,Hoffmann M R.The role of metal ion dopants in quantum-sized TiO2:correlation between photoreactivity and charge carried recombination dynamics[J].J Phys Chem,1994,98(5):13669-13679.
[36] Asahi R,Morikawa T,Ohwaki T,et al.Visible-Light photocatalysis in nitrogen-doped titanium oxides[J].Science,2001,20(3):301-307.
[37]王振领,李敏,刘天学,等.TiO2膜的光敏化及灭菌活性研究[J].陕西师范大学学报(自然科学版),2002,3(30):87-89.
[38] Spanhel L,Weller H,Henglein A.Photochemistry of semiconductor colloids electron injection from illuminated CdS into attached TiO2and ZnO particles[J].J Am Chem Soc,1987,109:6632-6635.
© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号 地址：北京市海淀区学院路29号 邮编：100083 电话：办公室：(+86 10)66554848；文献借阅、咨询服务、科技查新：66554700 |