汽车用钢板电阻点焊工艺参数优化选择

详细信息    查看全文 | 推荐本文 |

英文篇名：Resistance spot welding parameters optimal selection for automotive steel plate 作者：唐科 ; 梁翠 ; 黄微晏 ; 黄靖 英文作者：TANG Ke;LIANG Cui;HUANG Weiyan;HUANG Jing;SAIC-GM-Wuling Automobile Co.,Ltd.,Chongqing Branch; 关键词：电阻点焊 ; 焊接工艺参数 ; 熔核尺寸 ; 焊接质量 英文关键词：resistance spot welding;;welding parameters;;nugget size;;welding quality 中文刊名：DHJI 英文刊名：Electric Welding Machine 机构：上汽通用五菱汽车股份有限公司重庆分公司; 出版日期：2017-11-20 出版单位：电焊机 年：2017 期：v.47;No.366 语种：中文; 页：DHJI201711044 页数：6 CN：11 ISSN：51-1278/TM 分类号：121-126

摘要

焊装车间多采用多层板搭接进行电阻电焊,而电阻电焊过程的不确定性因素较多。为了用较少的试验次数得到满足生产要求的试验结果,以板厚0.8 mm+1.4 mm+1.8 mm的三层低碳钢板搭接为研究对象,分析各因素对多层板材搭接焊点熔核质量的影响,获得了最优焊接工艺参数。试验结果表明:板厚为0.8 mm+1.4 mm+1.8 mm的三层低碳钢板搭接最佳焊接工艺参数为多脉冲软规范焊接参数,即三周波,焊接电流8.8/11.1/9.6 k A、焊接时间5/19/5 cyc、电极压力3 k N,得到各层搭接板之间熔核直径大于等于φ6 mm。
        In welding workshop,multi plate lapping is used to resistance welding usually,but so many uncertainty factors are there in welding process. In order to use less test times to meet production requirements and solve the welding nugget problem of multilayered panel lap,the optimizing welding parameter for 3 layer of low carbon steel plate with thickness of 0.8 mm+1.4 mm+1.8 mm was found in this paper. Experimental results show that: the welding current 9.6/8.8/11.1 k A,welding time 5/19/5 cycle,electrode pressure 3 k N is suitable for 3 layer of low carbon steel plate with thickness of 0.8 mm +1.4 mm +1.8 mm,multiple-pulse welding parameter is appropriate for multilayered panel lap,and diameter of nugget on each layer can achieve 6 mm.

引文

[1]沈洁,林浩磊,张延松,等.差强差厚三层板电阻电焊熔核尺寸的控制方法[J].焊接学报,2011,33(1):33-36.
    [2]Schreiber S.Investigation into three-member welding[J].Welding and Cutting,2001(53):252-259.
    [3]蔡洪能,王雅生,张占伟,等.汽车用钢板电阻电焊工艺参数优化选择方法[J].材料工程,2016(增刊1):304-309.
    [4]孙海涛,王爵丰,马强.电极压力对三层超厚高强度钢板电阻电焊质量的影响分析[J].热加工工艺,2017,46(3):235-237.
    [5]Nielsen C V,Friis K S,Zhang W,et al.Three-sheet spot welding of advanced high-strength steels[J].Welding Journal,2011,90(2):32-40.