摘要
探讨捻度与后区牵伸对含木棉纤维包芯纱性能的影响。通过制备5种不同细纱捻度、3种不同后区牵伸的赛络纺纺纱,并测试混纺纱的拉伸断裂性能、毛羽、条干CV值等性能,寻找最佳的捻度和后区牵伸工艺。结果表明:后区牵伸为1. 25倍,捻度为60捻/10 cm时,含木棉纤维混纺纱线的综合性能最好,因此含木棉纤维的双包芯纱线成功开发能够解决单包芯纱线强力不足而造成的面料纬向断裂强力不足、面料容易出现滑弹、接口等质量问题。
The effects of twists and draft in back zone on kapok fiber core-spun yarn property were discussed. Five kinds of different twists spun yarn and three kinds of different draft in back zone spun yarn were produced. The tensile property, hairiness and unevenness CV of the blended yarns were tested to find the best craft of twist and draft in back zone. The results showed that when the draft in back zone 1.25 and60 twist/10 cm, the property of kapok core-spun yarn was best. Therefore, the successful development of double core yarns containing kapok fiber can solve the quality problems caused by the insufficient strength of single core yarns, such as the insufficient weft breaking strength of fabrics and the easy occurrence of fabric slippage.
引文
[1]王思顺,徐仁利,刘涛,等.双丝包芯纱的生产及在牛仔面料中的应用[J].棉纺织技术,2014, 42(11):33-37.
[2]杨莉,毕松梅,洪钧.混纺比对木棉棉混纺纱性能的影响[J].棉纺织技术, 2013(1):30-32.
[3]刘梅城,洪杰,张曙光,等.木棉/粘胶/涤纶/银纤维长丝包芯纱的工艺探讨[J].现代纺织技术,2012, 20(2):38-39.
[4]李丹丹,权利军,金肖克,等.氨纶与双组分复合长丝/棉包芯纱的拉伸弹性[J].纺织学报,2017, 38(5):31-36.
[5]周思婕,范伟思,陈倩,等.亚麻/棉/木棉/粘胶嵌入式复合纱的纺制[J].轻纺工业与技术, 2017(2):1-5.