摘要
针对钽、铪分离多采用HF体系,易造成环境污染这一现状,以某牌号含钽、铪合金渣为原料,采用焙烧+浓硫酸浸出工艺对钽、铪的分离进行研究。试验表明,当合金渣与碳酸钠质量比为1∶1、焙烧温度1 000℃、浓硫酸与合金渣体积质量为1∶1、浸出时间1h时,钽、铪的分离效率最高,可实现钽与铪的有效分离。
Separation of tantalum and hafnium in HF system tends to cause environmental pollution.Separation of tantalum and hafnium from alloy slag containing tantalum and hafnium by roasting and leaching with concentrated sulfuric acid was studied.The results show that tantalum and hafnium can be effectively separated under the conditions including mass ratio of alloy slag to sodium carbonate of 1:1,roasting temperature of 1 000℃,liquid-solid ratio of concentrated sulfuric acid to alloy slag of 1:1,and leaching time of 1 h.
引文
[1]张卜升,许万祥,吴贤,等.合金渣中铪的MIBK萃取分离试验[J].有色金属(冶炼部分),2016(8):35-38.
[2]张卜升,许万祥,吴贤,等.合金渣中钛铪的离子交换分离研究[J].有色金属(冶炼部分),2015(6):55-58.
[3]张卜升,许万祥,陈姝晖,等.含钽合金渣中钽的回收[J].有色金属(冶炼部分),2014(9):47-50.
[4]行卫东,范兴祥,董海刚,等.废旧高温合金中硫酸浸出镍钴的动力学研究[J].稀有金属,2014,38(4):674-679.
[5]范兴祥,行卫东,董海刚,等.从废旧高温合金的硫酸浸出渣中浸出分离钨钼铼[J].过程工程学报,2013,13(6):969-973.
[6]韩寿波,张义文.铪在粉末冶金高温合金中的作用研究概况[J].粉末冶金工业,2009,19(5):48-55.
[7]王治钧,王靖坤,陈昆昆,等.废旧高温合金中钽回收工艺的研究[J].有色金属(冶炼部分),2014(6):46-48.
[8]张秋月,郑国经.ICP-AES法测定高温合金中钽的研究[J].冶金分析,2005,25(4):25-29.
[9]张文杰,吴明,徐志高,等.DIBK-P350和DIBK-TOPO负载有机相中铪和锆的反萃[J].有色金属(冶炼部分),2018(5):41-45.
[10]刘珍珍,刘勇,刘牡丹,等.负载钽铌有机相中悬浮物的离心分离研究[J].有色金属(冶炼部分),2018(1):48-51.