通过立式喷涂生产线考察了航空用柱段结构产品自动喷涂有机硅涂层时的工艺参数。结果表明,喷涂压力为0.4~0.6 MPa,涂料流量为500~600 mL/min,喷涂距离为200~220 mm,喷枪摆动角度为45°~50°时,所得涂层厚度均匀,外观质量较好。
The process parameters for automatic spraying of silicone coating on the products with cylindrical structure used for aviation were studied on a vertical spraying production line. The results showed that the coatings obtained under the following conditions had a uniform thickness and good appearance: spray pressure 0.4-0.6 MPa, paint flow rate500-600 mL/min, nozzle-to-substrate distance 200-220 mm, and swing angle of spray gun 45°-50°.
引文
[1]傅绍燕.涂装工艺及车间设计手册[M].北京:机械工业出版社,2013:1-100.
[2]陈治良.现代涂装手册[M].北京:化学工业出版社,2010:1-20.
[3]李文胜,丁荥中.SAMES自动喷涂系统在汽车喷涂中的应用[J].电镀与涂饰,2007,26(12):42-44,54.
[4]章跃辉.汽车涂装生产技术新动向[J].电镀与涂饰,2009,28(4):67-71.
[5]姜峰.浅谈汽车涂装机器人[J].电镀与涂饰,1993,12(4):64-67.
[6]高文化,和军强.汽车车身内表面喷涂技术的应用[J].电镀与涂饰,2016,35(22):1194-1199.
[7]霍志磊,朱学军.自动导引车用电池壳体机器人喷涂工艺的设计[J].电镀与涂饰,2018,37(20):915-921.
[8]陈磊,陈桂林,刘武,等.汽车PVC自动喷涂胶雾控制[J].现代制造技术与装备,2015(5):140-141.
[9]王国磊,伊强,缪东晶,等.面向机器人喷涂的多变量涂层厚度分布模型[J].清华大学学报(自然科学版),2017,57(3):324-330.
[10]王国磊,陈恳,陈雁,等.变参数下的空气喷枪涂层厚度分布建模[J].吉林大学学报(工学版),2012,42(1):188-192.
[11]吴春龙,李统宇.喷涂机器人在造型生产线上的应用[J].现代铸铁,2017,37(3):77-80.
[12]谷昭斌.车身表面漆膜厚度的控制[J].汽车工艺与材料,2011(5):21-24.