卤氧化铋薄膜的制备及其在海洋防污应用中的进展
|
摘要
海洋生物污损引起的一系列经济损失和安全问题,是海洋开发过程中必须面临的重要问题之一,因此开发新型高效的防污技术具有重要意义。随着光催化抗污技术的发展,其在海洋防污的应用受到了广大研究者的关注。卤氧化铋(BiOX,X=Cl、Br、I)薄膜作为一种新型半导体薄膜,由于具有优异光催化性能、较高的机械强度和易于回收等优点,而成为应用于光催化防污领域中新的研究热点。综述了BiOX半导体薄膜的制备方法及其应用领域的最新进展。首先,在海洋污损与现存防污技术的研究背景下,概述了光催化技术应用于海洋防污的潜力。其次,综述了国内外当前BiOX薄膜制备技术及其应用领域,并介绍了各种方法的优缺点。之后总结了BiOX半导体膜在海洋防污领域的最新应用研究,其中特别强调了海洋环境中膜材料应用的必要性。最后,展望了BiOX半导体薄在海洋防污领域的发展前景,概述了可能产生突破性研究成果的发展方向,为进一步将BiOX薄膜应用于海洋防污领域打开了新的视角。
A series of economic losses and safety problems caused by marine biofouling are the important issues faced in the marine development. Therefore, the development of new and efficient anti-fouling technology is of great significance. With the development of photocatalytic antifouling technology, its application in marine antifouling has attracted the attention of researchers. As a new type of semiconductor film, bismuth oxyhalide(BiOX, X=Cl,Br,I) film has become a new research hotspot in the field of photocatalytic antifouling due to excellent photocatalytic performance, high mechanical strength and easy recycling. The work summarized BiOX film preparation technology and the recent advances in application. Firstly, the potential application of photocatalytic technology in Marine pollution prevention was summarized under the background of marine biofouling and existing anti-fouling technology. Secondly, BiOX thin film preparation technology at home and abroad and corresponding application fields were summarized, and the advantages and disadvantages of various methods were introduced. Later, the latest application research of BiOX semiconductor film in marine anti-fouling field was concluded, in which the necessity of film application in marine environment was highlighted. Finally, the perspective on the future development of BiOX semiconductor thin films in marine anti-fouling field was expected and the possible direction to yield breakthrough was outlined to open a new perspective for further application of BiOX thin films in marine anti-fouling field.
A series of economic losses and safety problems caused by marine biofouling are the important issues faced in the marine development. Therefore, the development of new and efficient anti-fouling technology is of great significance. With the development of photocatalytic antifouling technology, its application in marine antifouling has attracted the attention of researchers. As a new type of semiconductor film, bismuth oxyhalide(BiOX, X=Cl,Br,I) film has become a new research hotspot in the field of photocatalytic antifouling due to excellent photocatalytic performance, high mechanical strength and easy recycling. The work summarized BiOX film preparation technology and the recent advances in application. Firstly, the potential application of photocatalytic technology in Marine pollution prevention was summarized under the background of marine biofouling and existing anti-fouling technology. Secondly, BiOX thin film preparation technology at home and abroad and corresponding application fields were summarized, and the advantages and disadvantages of various methods were introduced. Later, the latest application research of BiOX semiconductor film in marine anti-fouling field was concluded, in which the necessity of film application in marine environment was highlighted. Finally, the perspective on the future development of BiOX semiconductor thin films in marine anti-fouling field was expected and the possible direction to yield breakthrough was outlined to open a new perspective for further application of BiOX thin films in marine anti-fouling field.
引文
[1]张盾,王毅,王鹏,等.海水环境生物腐蚀污损与防护[J].装备环境工程,2016,13(4):22-27.ZHANG Dun,WANG Yi,WANG Peng,et al.Biocorrosion and biofouling in seawater and their Protection[J].Equipment environmental engineering,2016,13(4):22-27.
[2]YEBRA D M,KIIL S,KIM D G.Antifouling technology-past,present and future steps towards efficient and environmentally friendly antifouling coatings[J].Progress in organic coatings,2004,50(2):75-104.
[3]LEWIN R.Microbial adhesion is a sticky problem[J].Science,1984,224(4647):375-377.
[4]COUTTS A D M,VALENTINE J P,EDGAR G J,et al.Removing vessels from the water for biofouling treatment has the potential to introduce mobile non-indigenous marine species[J].Marine pollution bulletin,2010,60(9):1533-1540.
[5]庆宜,马春风,张广照.海洋防污材料[J].科学,2017,69(1):27-31.QING Yi,MA Chun-feng,ZHANG Guang-zhao.Marine antifouling materials[J].science,2017,69(1):27-31.
[6]SCHULTZ M P,BENDICK J A,HOLM E R,et al.Economic impact of biofouling on a naval surface ship[J].Biofouling,2011,27(1):87-98.
[7]王珊珊,张瑞标,刘振华,等.海洋污损生物附着及防除途径[J].河北渔业,2016(11):42-45.WANG Shan-shan,ZHANG Rui-biao,LIU Zhen-hua,et al.Marine fouling organisms adhesion and prevention[J].Hebei fisheries,2016(11):42-45.
[8]BANERJEE I,PANGULE R C,KANE R S.Antifouling coatings:Recent developments in the design of surfaces that prevent fouling by proteins,bacteria,and marine organisms[J].Advanced materials,2011,23(6):690-718.
[9]PIOLA R F,DAFFORN K A,JOHNSTON E L.The influence of antifouling practices on marine invasions[J].Biofouling,2009,25(7):633-644.
[10]李军威,田俊杰,马光皎.电解防污技术及其实际应用情况探析[J].全面腐蚀控制,2015,29(10):44-47.LI Jun-wei,TIAN Jun-jie,MA Guang-jiao.Electrolytic anti-fouling system and actual applying cases analysis[J].Total corrosion control,2015,29(10):44-47.
[11]CRISTIANI P,PERBONI G.Antifouling strategies and corrosion control in cooling circuits[J].Bioelectrochemistry,2014,97(1):120-126.
[12]付大海,曹京宜.舰船涂料的发展趋势[J].中国涂料2003,18(1):49-53.FU Da-hai,CAO Jing-yi.Development trend of ship coatings[J].China coating,2003,18(1):49-53.
[13]CHAMBERS L D,STOKES,K R,WALSH F C,et al.Modern approaches to marine antifouling coatings[J].Surface and coatings technology,2006,201(6):3642-3652.
[14]MORA S J D,STEWART C,PHILLIPS D.Sources and rate of degradation of tri(N-butyl)tin in marine sediments near auckland,New Zealand[J].Marine pollution bulletin,1995,30(1):50-57.
[15]刘丽萍,曹秀凤.环境友好型海洋防污涂层的研究进展[J].材料导报,2014,28(23):355-357.LIU Li-ping,CAO Xiu-feng.Development of environmental friendly marine antifouling coatings[J].Materials review,2014,28(23):355-357.
[16]HU Z,FINLAY J A,CHEN L,et al.Photochemically cross-linked perfluoropolyether-based elastomers:Synthesis,physical characterization,and biofouling evaluation[J].Macromolecules,2009,42(18):6999-7007.
[17]MATSUNAGA T,TOMODA R,NAKAJIMA T,et al.Continuous-sterilization system that uses photosemiconductor powders[J].Appllied and environmental microbiology,1988,54(6):1330-1333.
[18]TOKODE O,PRABHU R,LAWTON L A,et al.Controlled periodic illumination in semiconductor photocatalysis[J].Journal of photochemistry and photobiology Achemistry,2016,319-320:96-106.
[19]LEE J H,KANG M,CHOUNG S J,et al.The preparation of TiO2 nanometer photocatalyst film by a hydrothermal method and its sterilization performance for giardia lamblia[J].Water research,2004,38(3):713-719.
[20]BUECHLER K J,ZAWISTOWSKI T M,NOBLE R D,et al.Investigation of the mechanism for the controlled periodic illumination effect in TiO2 photocatalysis[J].Industrial&engineering chemistry research,2001,40(4):1097-1102.
[21]PELAEZ M,NOLAN N T,PILLAI S C,et al.A review on the visible light active titanium dioxide photocatalysts for environmental applications[J].Applied catalysis B environmental,2012,125(33):331-349.
[22]GAO M,AN T,LI G,et al.Genetic studies of the role of fatty acid and coenzyme A in photocatalytic inactivation of escherichia coli[J].Water research,2012,46(13):3951-3957.
[23]CAO J,XU B,LUO B,et al.Preparation,characterization and visible-light photocatalytic activity of AgI/AgCl/TiO2[J].Applied surface science,2011,257(16):7083-7089.
[24]CHEN L,JIANG D,HE T,et al.In-situ ion exchange synthesis of hierarchical Ag I/Bi OI microsphere photocatalyst with enhanced photocatalytic properties[J].Crystengcomm,2013,15(37):7556-7563.
[25]SAITO T,IWASE T,HORIE J,et al.Mode of photocatalytic bactericidal action of powdered semiconductor TiO2on mutans streptococci[J].Journal of Photochemistry&photobiology B biology,1992,14(4):369-379.
[26]ZHANG L S,WONG K H,YIP H Y,et al.Effective photocatalytic disinfection of E.coli K-12 using Ag Br-Ag-Bi2WO6 nanojunction system irradiated by visible light:The role of diffusing hydroxyl radicals[J].Environmental science and technology,2010,44(4):1392-1398.
[27]CAI L.Chemical oxidation and DNA damage catalysed by inorganic sunscreen ingredients[J].Febs letters,1997,418(1-2):87-90.
[28]YUAN R,CHEN T,FEI E,et al.Surface chlorination of TiO2-based photocatalysts:A way to remarkably improve photocatalytic activity in both UV and visible region[J].ACS catalysis,2013,1(3):200-206.
[29]LIU S,YU J,JARONIEC M.Anatase TiO2 with dominant high-energy{001}facets:Synthesis,properties and applications[J].Chemistry of materials,2011,23(18):4085-4093.
[30]KUBACKA A,FERNáNDEZGARCíA M,COLóN G.Advanced nanoarchitectures for solar photocatalytic applications[J].Chemical reviews,2016,112(3):1555-1614.
[31]ASAHI R,MORIKAWA T,OHWAKI T,et al.Visible-light photocatalysis in nitrogen-doped titanium oxides[J].Science,2001,293(5528):269-71.
[32]SONG J,WANG X,YAN J,et al.Soft Zr-doped TiO2nanofibrous membranes with enhanced photocatalytic activity for water purification[J].Scientific reports,2017,7(1):1-12.
[33]HU Y,LI D,ZHENG Y,et al.BiVO4/TiO2 nanocrystalline heterostructure:A wide spectrum responsive photocatalyst towards the highly efficient decomposition of gaseous benzene[J].Applied catalysis B environmental,2011,104(1):30-36.
[34]YE L,SU Y,JIN X,et al.Recent advances in BiOX(X=Cl,Br and I)photocatalysts:Synthesis,modification,facet effects and mechanisms[J].Environmental science nano,2014,1(2):90-112.
[35]WANG G,LUO X,HUANG Y,et al.Bi OX/Bi OY(X,Y=F,Cl,Br,I)superlattices for visible light photocatalysis applications[J].RSC advances,2016,6(94):91508-91516.
[36]ZHANG X,AI Z,JIA F,et al.Generalized One-pot synthesis,characterization,and photocatalytic activity of hierarchical BiOX(X=Cl,Br,I)nanoplate microspheres[J].Journal of physical chemistry C,2008,112(3):747-753.
[37]BHACHU D S,MONIZ S J A,SATHASIVAM S,et al.Bismuth oxyhalides:Synthesis,structure and photoelectrochemical activity[J].Chemical science,2016,7(8):4832-4841.
[38]PARE B,SARWAN B,JONNALAGADDA S B.Photocatalytic mineralization study of malachite green on the surface of Mn-doped BiOCl activated by visible light under ambient condition[J].Applied surface science,2011,258(1):247-253.
[39]SHANG M,WANG W Z,ZHANG L.Preparation of BiOBr lamellar structure with high photocatalytic activity by CTAB as Br source and template[J].Journal of hazardous materials,2009,167(1):803-809.
[40]JIANG J,ZHAO K,XIAO X,et al.Synthesis and facet-dependent photoreactivity of Bi OCl single-crystalline nanosheets[J].Journal of the american chemical society,2012,134(10):4473-4476.
[41]HENLE J,SIMON P,FRENZEL A,et al.Nanosized BiOX(X=Cl,Br,I)particles synthesized in reverse microemulsions[J].Chemistry of materials,2007,19(3):366-373.
[42]MU Q,ZHANG Q,WANG H,et al.Facile growth of vertically aligned BiOCl nanosheet arrays on conductive glass substrate with high photocatalytic properties[J].Journal of materials chemistry,2012,22(33):16851.
[43]CAO S,GUO C,LYU Y,et al.A novel BiOCl film with flowerlike hierarchical structures and its optical properties[J].Nanotechnology,2009,20(27):275702.
[44]WU S,WANG C,CUI Y.Controllable growth of BiOCl film with high percentage of exposed{001}facets[J].Applied surface science,2014,289:266-273.
[45]ZHANG X,LIU X,FAN C,et al.A novel BiOCl thin film prepared by electrochemical method and its application in photocatalysis[J].Applied catalysis B:Environmental,2013,132-133:332-341.
[46]LI Y,LIU J,JIANG J,et al.UV-resistant superhydrophobic BiOCl nanoflake film by a room-temperature hydrolysis process[J].Dalton trans,2011,40(25):6632.
[47]CUI S,SHAN G,ZHU L.Solvothermal synthesis of I-deficient BiOI thin film with distinct photocatalytic activity and durability under simulated sunlight[J].Applied catalysis B:Environmental,2017,219:249-258.
[48]WANG M,GAO J,ZHU G,et al.One-step solvothermal synthesis of Fe-doped Bi OI film with enhanced photocatalytic performance[J].RSC advances,2016,108:106615-106624.
[49]WANG Y,LONG Y,ZHANG D.Facile in situ growth of high strong BiOI network films on metal wire meshes with photocatalytic activity[J].ACS sustainable chemistry&engineering,2017,5(3):2454-2462.
[50]WANG K,JIA F,ZHENG Z,et al.Crossed Bi OI flake array solar cells[J].Electrochemistry communications,2010,12(12):1764-1767.
[51]KAZYREVICH M E,MALASHCHONAKМV,MAZ-ANIK A V,et al.Photocurrent switching effect on plateletlike BiOI electrodes:Influence of redox system,light wavelength and thermal treatment[J].Electrochimica acta,2016,190:612-619.
[52]GAN J,RAJEEVA B B,WU Z,et al.Hydrogen-reduced bismuth oxyiodide nanoflake arrays with plasmonic enhancements for efficient photoelectrochemical water reduction[J].Electrochimica acta,2016,219:20-27.
[53]YE L,CHEN J,TIAN L,et al.BiOI thin film via chemical vapor transport:Photocatalytic activity,durability,selectivity and mechanism[J].Applied catalysis B:Environmental,2013,130-131:1-7.
[54]HAHN N T,HOANG S,SELF J L,et al.Spray pyrolysis deposition and photoelectrochemical properties of n-type Bi OI nanoplatelet thin films[J].ACS nano,2012,6(9):7712.
[55]HUO Y,HOU R,CHEN X,et al.Bi OBr visible-light photocatalytic films in a rotating disk reactor for the degradation of organics[J].Journal of materials chemistry A,2015,3(28):14801-14808.
[56]HOU R,GAO Y,ZHU H,et al.Coupling system of Ag/Bi OBr photocatalysis and direct contact membrane distillation for complete purification of N-containing dye wastewater[J].Chemical engineering journal,2017,317:386-393.
[57]LIU Z,WU B,NIU J,et al.Solvothermal synthesis of BiOBr thin film and its photocatalytic performance[J].Applied surface science,2014,288:369-372.
[58]JIA Y,YANG Y,GUO Y,et al.Simulated sunlight photocatalytic degradation of aqueous p-nitrophenol and bisphenol A in a Pt/BiOBr film-coated quartz fiber photoreactor[J].Dalton trans,2015,44(20):9439-9449.
[59]HU Y,LI R,FAN C,et al.One-step synthesis of porous Bi OBr film and Bi nanopowder simultaneously from Bi plate via electrochemical method[J].Materials letters,2015,161:41-44.
[60]LI K,ZHANG H,TANG Y,et al.Photocatalytic degradation and electricity generation in a rotating disk photoelectrochemical cell over hierarchical structured BiOBr film[J].Applied catalysis B:Environmental,2015,164:82-91.
[61]CUELLAR E L,MARTíNEZ-DE L C A,TORRES N C,et al.Deposition of BiOBr thin films by thermal evaporation and evaluation of its photocatalytic activity[J].Catalysis today,2015,252:2-6.
[62]LI L,ZHANG M,LIU Y,et al.Direct gowth of bismuth oxyhalides nanosheet arrays on carbon cloth for recycled photocatalytic degradation of dye and 4-nitrophenol[J].Nano,2015,10(5):1550066.
[63]LIU Z,RAN H,WU B,et al.Synthesis and characterization of Bi OI/Bi OBr heterostructure films with enhanced visible light photocatalytic activity[J].Colloids and surfaces A:Physicochemical and engineering aspects,2014,452:109-114.
[64]YIN H,CHEN X,HOU R,et al.Ag/BiOBr film in a rotating-disk reactor containing long-afterglow phosphor for round-the-clock photocatalysis[J].ACS applied materials interfaces,2015,7(36):20076-20082.
[65]CONG Y,JI Y,GE Y,et al.Fabrication of 3D Bi2O3-BiOIheterojunction by a simple dipping method:Highly enhanced visible-light photoelectrocatalytic activity[J].Chemical engineering journal,2017,307:572-582.
[66]ZHANG K L,LIU C M,HUANG F Q,et al.Study of the electronic structure and photocatalytic activity of the Bi OCl photocatalyst[J].Applied catalysis B:Environmental,2006,68(3):125-129.
[67]王云燕,彭文杰,柴立元,等.硝酸铋转化水解法制备片状Bi OCl粉末的研究[J].金属材料与冶金工程,2003,31(3):20-23.WANG Yun-yan,PENG Wen-jie,CHAI Li-yuan,et al.Study on preparation of sheet BiOCl powder by the method of bismuth nitrate transformation and hydrolysis[J].Metal materials and metallurgy engineering,2003,31(3):20-23.
[68]BENABBOU A K,DERRICHE Z,FELIX C,et al.Photocatalytic inactivation of escherischia coli:Effect of concentration of TiO2 and microorganism,nature,and intensity of UV irradiation[J].Applied catalysis B environmental,2007,76(3):257-263.
[69]CHEN F,YANG X,WU Q.Photocatalytic oxidation of escherischia coli,aspergillus niger,and formaldehyde under different ultraviolet irradiation conditions[J].Environmental science&technology,2009,43(12):4606-4611.
[70]KRYSA J,MUSILOVáE,ZITA J.Critical assessment of suitable methods used for determination of antibacterial properties at photocatalytic surfaces[J].Journal of hazardous materials,2011,195(1):100-106.
[71]PELLER J R,WHITMAN R L,GRIFFITH S,et al.TiO2as a photocatalyst for control of the aquatic invasive alga cladophora,under natural and artificial light[J].Journal of photochemistry&photobiology A chemistry,2007,186(2):212-217.
[72]SUNADA K,WATANABE T,HASHIMOTO K.Studies on photokilling of bacteria on TiO2 thin film[J].Journal of photochemistry and photobiology A:Chemistry,2003,156(1):227-233.
[73]SINGH A,DUTTA D P,BALLAL A,et al.Visible light driven photocatalysis and antibacterial activity of AgVO3and Ag/AgVO3 nanowires[J].Materials research bulletin2014,51:447-454.
[74]WANG W,YU J C,XIA D,et al.Graphene and g-C3N4nanosheets cowrapped elementalα-Sulfur as a novel metal-free heterojunction photocatalyst for bacterial inactivation under visible-light[J].Environmental science&technology,2013,47(15):8724-8732.
[75]JAMIL T S,MANSOR E S,AZAB EL-LIETHY M.Photocatalytic inactivation of E.coli using nano-size bismuth oxyiodide photocatalysts under visible light[J].Journal of environmental chemical engineering,2015,3(4):2463-2471.
[76]ZHANG D,WEN M,JIANG B,et al.Ionothermal synthesis of hierarchical BiOBr microspheres for water treatment[J].Journal of hazardous materials,2012211-212:104-111.
[77]WU D,WANG B,WANG W,et al.Visible-light-driven Bi OBr nanosheets for highly facet-dependent photocatalytic inactivation of Escherichia coli[J].Journal of materials chemistry A,2015,3(29):15148-15155.
[78]WU D,YUE S,WANG W,et al.Boron doped Bi OBr nanosheets with enhanced photocatalytic inactivation of escherichia coli[J].Applied catalysis B:Environmental,2016,192:35-45.
[79]WEI D,TIAN F,LU Z,et al.Facile synthesis of Ag/AgCl/BiOCl temary nanocomposites for photocatalytic inactivation of S.aureus under visible light[J].RSCadvances,2016,6(57):52264-52270.
[80]WANG Y,LIN L,LI F,et al.Enhanced photocatalytic bacteriostatic activity towards escherichia coli using 3Dhierarchical microsphere BiOI/BiOBr under visible light irradiation[J].Photochemical&photobiological sciences,2016,15(5):666-672.
[81]JU P,WANG P,LI B,et al.A novel calcined Bi2WO6/Bi VO4heterojunction photocatalyst with highly enhanced photocatalytic activity[J].Chemical engineering journal,2014,236(2):430-437.
[82]XIANG Z,WANG Y,ZHANG D,et al.BiOI/BiVO4 p-n heterojunction with enhanced photocatalytic activity under visible-light irradiation[J].Journal of industrial and engineering chemistry,2016,40:83-92.
[83]XIANG Z,WANG Y,JU P,et al.Controlled synthesis and photocatalytic antifouling properties of BiVO4 with tunable morphologies[J].Journal of electronic materials,2017,46(2):758-765.
[84]LONG Y,WANG Y,ZHANG D,et al.Facile synthesis of BiOI in hierarchical nanostructure preparation and its photocatalytic application to organic dye removal and biocidal effect of bacteria[J].Journal of colloid and interface science,2016,481:47-56.
[85]XIANG Y,JU P,WANG Y,et al.Chemical etching preparation of the Bi2WO6/BiOI p-n heterojunction with enhanced photocatalytic antifouling activity under visible light irradiation[J].Chemical engineering journal,2016288:264-275.
[86]WAN Y,ZHANG D,WANG Y,et al.Vancomycin-functionalised Ag@TiO2 phototoxicity for bacteria[J].Journal of hazardous materials,2011,186(1):306-312.
[87]WANG Y,LONG Y,YANG Z.A novel ion-exchange strategy for the fabrication of high strong BiOI/BiOBr heterostructure film coated metal wire mesh with tunable visible-light-driven photocatalytic reactivity[J].Journal of hazardous materials,2018,351(5):11-19.
[2]YEBRA D M,KIIL S,KIM D G.Antifouling technology-past,present and future steps towards efficient and environmentally friendly antifouling coatings[J].Progress in organic coatings,2004,50(2):75-104.
[3]LEWIN R.Microbial adhesion is a sticky problem[J].Science,1984,224(4647):375-377.
[4]COUTTS A D M,VALENTINE J P,EDGAR G J,et al.Removing vessels from the water for biofouling treatment has the potential to introduce mobile non-indigenous marine species[J].Marine pollution bulletin,2010,60(9):1533-1540.
[5]庆宜,马春风,张广照.海洋防污材料[J].科学,2017,69(1):27-31.QING Yi,MA Chun-feng,ZHANG Guang-zhao.Marine antifouling materials[J].science,2017,69(1):27-31.
[6]SCHULTZ M P,BENDICK J A,HOLM E R,et al.Economic impact of biofouling on a naval surface ship[J].Biofouling,2011,27(1):87-98.
[7]王珊珊,张瑞标,刘振华,等.海洋污损生物附着及防除途径[J].河北渔业,2016(11):42-45.WANG Shan-shan,ZHANG Rui-biao,LIU Zhen-hua,et al.Marine fouling organisms adhesion and prevention[J].Hebei fisheries,2016(11):42-45.
[8]BANERJEE I,PANGULE R C,KANE R S.Antifouling coatings:Recent developments in the design of surfaces that prevent fouling by proteins,bacteria,and marine organisms[J].Advanced materials,2011,23(6):690-718.
[9]PIOLA R F,DAFFORN K A,JOHNSTON E L.The influence of antifouling practices on marine invasions[J].Biofouling,2009,25(7):633-644.
[10]李军威,田俊杰,马光皎.电解防污技术及其实际应用情况探析[J].全面腐蚀控制,2015,29(10):44-47.LI Jun-wei,TIAN Jun-jie,MA Guang-jiao.Electrolytic anti-fouling system and actual applying cases analysis[J].Total corrosion control,2015,29(10):44-47.
[11]CRISTIANI P,PERBONI G.Antifouling strategies and corrosion control in cooling circuits[J].Bioelectrochemistry,2014,97(1):120-126.
[12]付大海,曹京宜.舰船涂料的发展趋势[J].中国涂料2003,18(1):49-53.FU Da-hai,CAO Jing-yi.Development trend of ship coatings[J].China coating,2003,18(1):49-53.
[13]CHAMBERS L D,STOKES,K R,WALSH F C,et al.Modern approaches to marine antifouling coatings[J].Surface and coatings technology,2006,201(6):3642-3652.
[14]MORA S J D,STEWART C,PHILLIPS D.Sources and rate of degradation of tri(N-butyl)tin in marine sediments near auckland,New Zealand[J].Marine pollution bulletin,1995,30(1):50-57.
[15]刘丽萍,曹秀凤.环境友好型海洋防污涂层的研究进展[J].材料导报,2014,28(23):355-357.LIU Li-ping,CAO Xiu-feng.Development of environmental friendly marine antifouling coatings[J].Materials review,2014,28(23):355-357.
[16]HU Z,FINLAY J A,CHEN L,et al.Photochemically cross-linked perfluoropolyether-based elastomers:Synthesis,physical characterization,and biofouling evaluation[J].Macromolecules,2009,42(18):6999-7007.
[17]MATSUNAGA T,TOMODA R,NAKAJIMA T,et al.Continuous-sterilization system that uses photosemiconductor powders[J].Appllied and environmental microbiology,1988,54(6):1330-1333.
[18]TOKODE O,PRABHU R,LAWTON L A,et al.Controlled periodic illumination in semiconductor photocatalysis[J].Journal of photochemistry and photobiology Achemistry,2016,319-320:96-106.
[19]LEE J H,KANG M,CHOUNG S J,et al.The preparation of TiO2 nanometer photocatalyst film by a hydrothermal method and its sterilization performance for giardia lamblia[J].Water research,2004,38(3):713-719.
[20]BUECHLER K J,ZAWISTOWSKI T M,NOBLE R D,et al.Investigation of the mechanism for the controlled periodic illumination effect in TiO2 photocatalysis[J].Industrial&engineering chemistry research,2001,40(4):1097-1102.
[21]PELAEZ M,NOLAN N T,PILLAI S C,et al.A review on the visible light active titanium dioxide photocatalysts for environmental applications[J].Applied catalysis B environmental,2012,125(33):331-349.
[22]GAO M,AN T,LI G,et al.Genetic studies of the role of fatty acid and coenzyme A in photocatalytic inactivation of escherichia coli[J].Water research,2012,46(13):3951-3957.
[23]CAO J,XU B,LUO B,et al.Preparation,characterization and visible-light photocatalytic activity of AgI/AgCl/TiO2[J].Applied surface science,2011,257(16):7083-7089.
[24]CHEN L,JIANG D,HE T,et al.In-situ ion exchange synthesis of hierarchical Ag I/Bi OI microsphere photocatalyst with enhanced photocatalytic properties[J].Crystengcomm,2013,15(37):7556-7563.
[25]SAITO T,IWASE T,HORIE J,et al.Mode of photocatalytic bactericidal action of powdered semiconductor TiO2on mutans streptococci[J].Journal of Photochemistry&photobiology B biology,1992,14(4):369-379.
[26]ZHANG L S,WONG K H,YIP H Y,et al.Effective photocatalytic disinfection of E.coli K-12 using Ag Br-Ag-Bi2WO6 nanojunction system irradiated by visible light:The role of diffusing hydroxyl radicals[J].Environmental science and technology,2010,44(4):1392-1398.
[27]CAI L.Chemical oxidation and DNA damage catalysed by inorganic sunscreen ingredients[J].Febs letters,1997,418(1-2):87-90.
[28]YUAN R,CHEN T,FEI E,et al.Surface chlorination of TiO2-based photocatalysts:A way to remarkably improve photocatalytic activity in both UV and visible region[J].ACS catalysis,2013,1(3):200-206.
[29]LIU S,YU J,JARONIEC M.Anatase TiO2 with dominant high-energy{001}facets:Synthesis,properties and applications[J].Chemistry of materials,2011,23(18):4085-4093.
[30]KUBACKA A,FERNáNDEZGARCíA M,COLóN G.Advanced nanoarchitectures for solar photocatalytic applications[J].Chemical reviews,2016,112(3):1555-1614.
[31]ASAHI R,MORIKAWA T,OHWAKI T,et al.Visible-light photocatalysis in nitrogen-doped titanium oxides[J].Science,2001,293(5528):269-71.
[32]SONG J,WANG X,YAN J,et al.Soft Zr-doped TiO2nanofibrous membranes with enhanced photocatalytic activity for water purification[J].Scientific reports,2017,7(1):1-12.
[33]HU Y,LI D,ZHENG Y,et al.BiVO4/TiO2 nanocrystalline heterostructure:A wide spectrum responsive photocatalyst towards the highly efficient decomposition of gaseous benzene[J].Applied catalysis B environmental,2011,104(1):30-36.
[34]YE L,SU Y,JIN X,et al.Recent advances in BiOX(X=Cl,Br and I)photocatalysts:Synthesis,modification,facet effects and mechanisms[J].Environmental science nano,2014,1(2):90-112.
[35]WANG G,LUO X,HUANG Y,et al.Bi OX/Bi OY(X,Y=F,Cl,Br,I)superlattices for visible light photocatalysis applications[J].RSC advances,2016,6(94):91508-91516.
[36]ZHANG X,AI Z,JIA F,et al.Generalized One-pot synthesis,characterization,and photocatalytic activity of hierarchical BiOX(X=Cl,Br,I)nanoplate microspheres[J].Journal of physical chemistry C,2008,112(3):747-753.
[37]BHACHU D S,MONIZ S J A,SATHASIVAM S,et al.Bismuth oxyhalides:Synthesis,structure and photoelectrochemical activity[J].Chemical science,2016,7(8):4832-4841.
[38]PARE B,SARWAN B,JONNALAGADDA S B.Photocatalytic mineralization study of malachite green on the surface of Mn-doped BiOCl activated by visible light under ambient condition[J].Applied surface science,2011,258(1):247-253.
[39]SHANG M,WANG W Z,ZHANG L.Preparation of BiOBr lamellar structure with high photocatalytic activity by CTAB as Br source and template[J].Journal of hazardous materials,2009,167(1):803-809.
[40]JIANG J,ZHAO K,XIAO X,et al.Synthesis and facet-dependent photoreactivity of Bi OCl single-crystalline nanosheets[J].Journal of the american chemical society,2012,134(10):4473-4476.
[41]HENLE J,SIMON P,FRENZEL A,et al.Nanosized BiOX(X=Cl,Br,I)particles synthesized in reverse microemulsions[J].Chemistry of materials,2007,19(3):366-373.
[42]MU Q,ZHANG Q,WANG H,et al.Facile growth of vertically aligned BiOCl nanosheet arrays on conductive glass substrate with high photocatalytic properties[J].Journal of materials chemistry,2012,22(33):16851.
[43]CAO S,GUO C,LYU Y,et al.A novel BiOCl film with flowerlike hierarchical structures and its optical properties[J].Nanotechnology,2009,20(27):275702.
[44]WU S,WANG C,CUI Y.Controllable growth of BiOCl film with high percentage of exposed{001}facets[J].Applied surface science,2014,289:266-273.
[45]ZHANG X,LIU X,FAN C,et al.A novel BiOCl thin film prepared by electrochemical method and its application in photocatalysis[J].Applied catalysis B:Environmental,2013,132-133:332-341.
[46]LI Y,LIU J,JIANG J,et al.UV-resistant superhydrophobic BiOCl nanoflake film by a room-temperature hydrolysis process[J].Dalton trans,2011,40(25):6632.
[47]CUI S,SHAN G,ZHU L.Solvothermal synthesis of I-deficient BiOI thin film with distinct photocatalytic activity and durability under simulated sunlight[J].Applied catalysis B:Environmental,2017,219:249-258.
[48]WANG M,GAO J,ZHU G,et al.One-step solvothermal synthesis of Fe-doped Bi OI film with enhanced photocatalytic performance[J].RSC advances,2016,108:106615-106624.
[49]WANG Y,LONG Y,ZHANG D.Facile in situ growth of high strong BiOI network films on metal wire meshes with photocatalytic activity[J].ACS sustainable chemistry&engineering,2017,5(3):2454-2462.
[50]WANG K,JIA F,ZHENG Z,et al.Crossed Bi OI flake array solar cells[J].Electrochemistry communications,2010,12(12):1764-1767.
[51]KAZYREVICH M E,MALASHCHONAKМV,MAZ-ANIK A V,et al.Photocurrent switching effect on plateletlike BiOI electrodes:Influence of redox system,light wavelength and thermal treatment[J].Electrochimica acta,2016,190:612-619.
[52]GAN J,RAJEEVA B B,WU Z,et al.Hydrogen-reduced bismuth oxyiodide nanoflake arrays with plasmonic enhancements for efficient photoelectrochemical water reduction[J].Electrochimica acta,2016,219:20-27.
[53]YE L,CHEN J,TIAN L,et al.BiOI thin film via chemical vapor transport:Photocatalytic activity,durability,selectivity and mechanism[J].Applied catalysis B:Environmental,2013,130-131:1-7.
[54]HAHN N T,HOANG S,SELF J L,et al.Spray pyrolysis deposition and photoelectrochemical properties of n-type Bi OI nanoplatelet thin films[J].ACS nano,2012,6(9):7712.
[55]HUO Y,HOU R,CHEN X,et al.Bi OBr visible-light photocatalytic films in a rotating disk reactor for the degradation of organics[J].Journal of materials chemistry A,2015,3(28):14801-14808.
[56]HOU R,GAO Y,ZHU H,et al.Coupling system of Ag/Bi OBr photocatalysis and direct contact membrane distillation for complete purification of N-containing dye wastewater[J].Chemical engineering journal,2017,317:386-393.
[57]LIU Z,WU B,NIU J,et al.Solvothermal synthesis of BiOBr thin film and its photocatalytic performance[J].Applied surface science,2014,288:369-372.
[58]JIA Y,YANG Y,GUO Y,et al.Simulated sunlight photocatalytic degradation of aqueous p-nitrophenol and bisphenol A in a Pt/BiOBr film-coated quartz fiber photoreactor[J].Dalton trans,2015,44(20):9439-9449.
[59]HU Y,LI R,FAN C,et al.One-step synthesis of porous Bi OBr film and Bi nanopowder simultaneously from Bi plate via electrochemical method[J].Materials letters,2015,161:41-44.
[60]LI K,ZHANG H,TANG Y,et al.Photocatalytic degradation and electricity generation in a rotating disk photoelectrochemical cell over hierarchical structured BiOBr film[J].Applied catalysis B:Environmental,2015,164:82-91.
[61]CUELLAR E L,MARTíNEZ-DE L C A,TORRES N C,et al.Deposition of BiOBr thin films by thermal evaporation and evaluation of its photocatalytic activity[J].Catalysis today,2015,252:2-6.
[62]LI L,ZHANG M,LIU Y,et al.Direct gowth of bismuth oxyhalides nanosheet arrays on carbon cloth for recycled photocatalytic degradation of dye and 4-nitrophenol[J].Nano,2015,10(5):1550066.
[63]LIU Z,RAN H,WU B,et al.Synthesis and characterization of Bi OI/Bi OBr heterostructure films with enhanced visible light photocatalytic activity[J].Colloids and surfaces A:Physicochemical and engineering aspects,2014,452:109-114.
[64]YIN H,CHEN X,HOU R,et al.Ag/BiOBr film in a rotating-disk reactor containing long-afterglow phosphor for round-the-clock photocatalysis[J].ACS applied materials interfaces,2015,7(36):20076-20082.
[65]CONG Y,JI Y,GE Y,et al.Fabrication of 3D Bi2O3-BiOIheterojunction by a simple dipping method:Highly enhanced visible-light photoelectrocatalytic activity[J].Chemical engineering journal,2017,307:572-582.
[66]ZHANG K L,LIU C M,HUANG F Q,et al.Study of the electronic structure and photocatalytic activity of the Bi OCl photocatalyst[J].Applied catalysis B:Environmental,2006,68(3):125-129.
[67]王云燕,彭文杰,柴立元,等.硝酸铋转化水解法制备片状Bi OCl粉末的研究[J].金属材料与冶金工程,2003,31(3):20-23.WANG Yun-yan,PENG Wen-jie,CHAI Li-yuan,et al.Study on preparation of sheet BiOCl powder by the method of bismuth nitrate transformation and hydrolysis[J].Metal materials and metallurgy engineering,2003,31(3):20-23.
[68]BENABBOU A K,DERRICHE Z,FELIX C,et al.Photocatalytic inactivation of escherischia coli:Effect of concentration of TiO2 and microorganism,nature,and intensity of UV irradiation[J].Applied catalysis B environmental,2007,76(3):257-263.
[69]CHEN F,YANG X,WU Q.Photocatalytic oxidation of escherischia coli,aspergillus niger,and formaldehyde under different ultraviolet irradiation conditions[J].Environmental science&technology,2009,43(12):4606-4611.
[70]KRYSA J,MUSILOVáE,ZITA J.Critical assessment of suitable methods used for determination of antibacterial properties at photocatalytic surfaces[J].Journal of hazardous materials,2011,195(1):100-106.
[71]PELLER J R,WHITMAN R L,GRIFFITH S,et al.TiO2as a photocatalyst for control of the aquatic invasive alga cladophora,under natural and artificial light[J].Journal of photochemistry&photobiology A chemistry,2007,186(2):212-217.
[72]SUNADA K,WATANABE T,HASHIMOTO K.Studies on photokilling of bacteria on TiO2 thin film[J].Journal of photochemistry and photobiology A:Chemistry,2003,156(1):227-233.
[73]SINGH A,DUTTA D P,BALLAL A,et al.Visible light driven photocatalysis and antibacterial activity of AgVO3and Ag/AgVO3 nanowires[J].Materials research bulletin2014,51:447-454.
[74]WANG W,YU J C,XIA D,et al.Graphene and g-C3N4nanosheets cowrapped elementalα-Sulfur as a novel metal-free heterojunction photocatalyst for bacterial inactivation under visible-light[J].Environmental science&technology,2013,47(15):8724-8732.
[75]JAMIL T S,MANSOR E S,AZAB EL-LIETHY M.Photocatalytic inactivation of E.coli using nano-size bismuth oxyiodide photocatalysts under visible light[J].Journal of environmental chemical engineering,2015,3(4):2463-2471.
[76]ZHANG D,WEN M,JIANG B,et al.Ionothermal synthesis of hierarchical BiOBr microspheres for water treatment[J].Journal of hazardous materials,2012211-212:104-111.
[77]WU D,WANG B,WANG W,et al.Visible-light-driven Bi OBr nanosheets for highly facet-dependent photocatalytic inactivation of Escherichia coli[J].Journal of materials chemistry A,2015,3(29):15148-15155.
[78]WU D,YUE S,WANG W,et al.Boron doped Bi OBr nanosheets with enhanced photocatalytic inactivation of escherichia coli[J].Applied catalysis B:Environmental,2016,192:35-45.
[79]WEI D,TIAN F,LU Z,et al.Facile synthesis of Ag/AgCl/BiOCl temary nanocomposites for photocatalytic inactivation of S.aureus under visible light[J].RSCadvances,2016,6(57):52264-52270.
[80]WANG Y,LIN L,LI F,et al.Enhanced photocatalytic bacteriostatic activity towards escherichia coli using 3Dhierarchical microsphere BiOI/BiOBr under visible light irradiation[J].Photochemical&photobiological sciences,2016,15(5):666-672.
[81]JU P,WANG P,LI B,et al.A novel calcined Bi2WO6/Bi VO4heterojunction photocatalyst with highly enhanced photocatalytic activity[J].Chemical engineering journal,2014,236(2):430-437.
[82]XIANG Z,WANG Y,ZHANG D,et al.BiOI/BiVO4 p-n heterojunction with enhanced photocatalytic activity under visible-light irradiation[J].Journal of industrial and engineering chemistry,2016,40:83-92.
[83]XIANG Z,WANG Y,JU P,et al.Controlled synthesis and photocatalytic antifouling properties of BiVO4 with tunable morphologies[J].Journal of electronic materials,2017,46(2):758-765.
[84]LONG Y,WANG Y,ZHANG D,et al.Facile synthesis of BiOI in hierarchical nanostructure preparation and its photocatalytic application to organic dye removal and biocidal effect of bacteria[J].Journal of colloid and interface science,2016,481:47-56.
[85]XIANG Y,JU P,WANG Y,et al.Chemical etching preparation of the Bi2WO6/BiOI p-n heterojunction with enhanced photocatalytic antifouling activity under visible light irradiation[J].Chemical engineering journal,2016288:264-275.
[86]WAN Y,ZHANG D,WANG Y,et al.Vancomycin-functionalised Ag@TiO2 phototoxicity for bacteria[J].Journal of hazardous materials,2011,186(1):306-312.
[87]WANG Y,LONG Y,YANG Z.A novel ion-exchange strategy for the fabrication of high strong BiOI/BiOBr heterostructure film coated metal wire mesh with tunable visible-light-driven photocatalytic reactivity[J].Journal of hazardous materials,2018,351(5):11-19.