摘要
在NaCl-KCl-NaF-NiO熔盐体系中,采用纯镍板为阳极,碳钢板为阴极,电沉积制备Fe-Ni功能材料,并结合SEM和EDS研究了电流密度和电流波形等因素对沉积层表面形貌的影响规律。结果表明,采用双向脉冲电流,电流密度30mA/cm2,在750℃电沉积50 min,可以得到致密、光滑的Fe-Ni梯度层。
Fe-Ni functional material was prepared by electrodeposition in NaCl-KCl-NaF-NiO molten salt system applying pure nickel plate as anode and carbon steel plate as cathode.Effects of current density and current waveform on surface morphology of sediment were studied with SEM and EDS.The results show that a dense,uniform Fe-Ni deposited layer is obtained under the conditions including bidirectional pulse current,current density of 30 mA/cm2,temperature of 750℃,and time of 50 min.
引文
[1]KANAHASHI H,MUKAI T,YAMADA Y,et al.Dynamic compression of an ultra-low density aluminium foam[J].Materials Science and Engineering.A:Structural Materials:Properties,Microstructure and Processing,2000,280(2):349-353.
[2]肖作安,费锡明,邹勇进.锌镍合金镀层耐腐蚀性的研究[J].材料保护,2005,38(03):15-19.
[3]张银亮,张传福,湛青,等.铁镍合金粉末的制备及研究现状[J].四川有色金属,2007,1(1):31-36.
[4]苏长伟.铁镍和金箔的电化学制备及其结构性能研究[D].长沙:湖南大学,2010.
[5]李运刚,李智慧,马瑞新,等.渗硅制备Mo-MoSi2梯度材料层的特性[J].稀有金属材料与工程,2008,37(11):1992-1995.
[6]李欣,李慧荣,马涛,等.钨的电化学还原机理及结晶过程研究[J].有色金属(冶炼部分),2019(1):59-63.
[7]SAEZ V,GRAVES J,PANIWNYK L,et al.Copper electrocrystallization on titanium electrodes:Controlled growth of copper nuclei using apotential step technique[J].Physics Procedia,2010,3(1):111-115.
[8]杨海丽.熔盐脉冲电沉积制备高硅钢的研究[D].河北秦皇岛:燕山大学,2010.