Temperature-Sensitive Polymersomes for Controlled Delivery of Anticancer Drugs

详细信息    查看全文

• 作者：Fei Liu ; Veronika Kozlovskaya ; Srikanth Medipelli ; Bing Xue ; Fahim Ahmad ; Mohammad Saeed ; Donald Cropek ; Eugenia Kharlampieva
• 刊名：Chemistry of Materials
• 出版年：2015
• 出版时间：December 8, 2015
• 年：2015
• 卷：27
• 期：23
• 页码：7945-7956
• 全文大小：771K
• ISSN：1520-5002

文摘

We report on a novel type of triblock copolymer polymersomes with temperature-controlled permeability within the physiologically relevant temperature range of 37鈥?2 掳C for sustained delivery of anticancer drugs. These polymersomes combine characteristics of liposomes, such as biocompatibility, biodegradability, monodispersity, and stability at room temperature, with tunable size and thermal responsiveness provided by amphiphilic triblock copolymers. The temperature-sensitive poly(N-vinylcaprolactam)_n-poly(dimethylsiloxane)₆₅-poly(N-vinylcaprolactam)_n (PVCL_n-PDMS₆₅-PVCL_n) copolymers with n = 10, 15, 19, 29, and 50 and polydispersity indexes less than 1.17 are synthesized by controlled RAFT polymerization. The copolymers are assembled into stable vesicles at room temperature when the ratio of PVCL to the total polymer mass is 0.36 < f < 0.52 with the polymersome diameter decreasing from 530 to 40 nm as the length of PVCL is increased from 10 to 19 monomer units. Importantly, the permeability of polymersomes loaded with the anticancer drug doxorubicin can be precisely controlled by PVCL length in the temperature range of 37鈥?2 掳C. Increasing the temperature above the lower critical solution temperature of PVCL results in either gradual vesicle shrinkage (n = 10 and n = 15) or reversible formation of beadlike aggregates with no size change (n = 19), both leading to sustained drug release. All temperature-triggered morphological changes are reversible and do not compromise the structural stability of the vesicles. Finally, concentration- and time-dependent cytotoxicity of drug-loaded polymersomes to human alveolar adenocarcinoma cells is demonstrated. Considering the high loading capacity (鈭?0%) and temperature responsiveness in the physiological range, these polymer vesicles have considerable potential as novel types of stimuli-responsive drug nanocarriers.