Shape memory response and mechanical properties of warm deformed NiTi intermetallic alloy

详细信息    查看全文

• 作者：M. Ataei ; A. Zarei-Hanzaki ; A. Shamsolhodaei
• 关键词：Thermomechanical processing ; NiTi shape memory alloy ; Shape memory effect ; Mechanical properties
• 刊名：Materials Science and Engineering: A
• 出版年：2017
• 出版时间：5 January 2017
• 年：2017
• 卷：680
• 期：Complete
• 页码：291-296
• 全文大小：1012 K
• 卷排序：680

文摘

The warm deformation method as an effective thermomechanical processing (TMP) route was applied on the equiatomic NiTi alloy to enhance its shape memory and mechanical properties. To this end, warm compression tests at different temperatures in the range of 100–500 °C under different strain rates of 0.003, 0.03 and 0.3 s−1 were performed. The material flow behaviors at 100 °C revealed the occurrence of stress induced martensite formation; this caused the specimens to fail by fracture. However, the material flow behavior at 300 °C and 500 °C demonstrated a dynamic restoration phenomenon. The higher stability of austenite phase in the processed specimens at 300 °C was indicated by microstructural and XRD analysis. In addition, the bimodal martensite packets were distinguished in the materials processed at 500 °C. The latter might well designate the occurrence of dynamic recrystallization phenomena. Furthermore these existence of austenite phase in 300 °C processed samples lead to an unfavorable shape memory response, while the fully martensitic structure of 500 °C processed samples materials exhibited a better shape memory recovery. The final mechanical properties of the alloy were improved through TMP, and applying the TMP at 500 °C increased the shape recovery strain of the alloy from approximately 1.5% (in as-hot rolled material) to 3.6%.