Comparison of the hot-stamped boron-alloyed steel and the warm-stamped medium-Mn steel on microstructure and mechanical properties

详细信息    查看全文

• 作者：Xiaodong Li<sup>asup> ; Ying Chang<sup>asup><sup> ; sup><sup>1sup><sup> ; sup><sup>yingc@dlut.edu.cn" class="auth_mail" title="E-mail the corresponding authorsup> ; Cunyu Wang<sup>bsup> ; Ping Hu<sup>asup> ; Han Dong<sup>bsup>
• 关键词：Medium-Mn steel ; Warm stamping ; Martensitic transformation ; Microstructure ; Mechanical properties ; Uniformity
• 刊名：Materials Science & Engineering A
• 出版年：2017
• 出版时间：2 January 2017
• 年：2017
• 卷：679
• 期：Complete
• 页码：240-248
• 全文大小：2824 K

文摘

The application of high strength steels (HSS) for automotive structural parts is an effective way to realize lightweight and enhance safety. Therefore, improvements in mechanical properties of HSS are needed. In the present study, the warm stamping process of the third generation automotive medium-Mn steel was discussed, the characteristics of martensitic transformation were investigated, as well as the microstructure and mechanical properties were analyzed, compared to the popular hot-stamped 22MnB5 steel in the automotive industry. The results are indicated as follows. Firstly, the quenching rate of the medium-Mn steel can be selected in a wide range based on its CCT curves, which is beneficial to the control of forming process. Secondly, the influence of stamping temperature and pressure on the M<sub>ssub> temperature of the medium-Mn steel is not obvious and can be neglected, which is favorable to the even distribution of martensitic microstructure and mechanical properties. Thirdly, the phenomenon of decarbonization is hardly found on the surface of the warm-stamped medium-Mn steel, and the ultra-fine-grained microstructure is found inside the medium-Mn steel after warm stamping. Besides, the warm-stamped medium-Mn steel holds the better comprehensive properties, such as a lower yield ratio, higher total elongation and higher tear toughness than the hot-stamped 22MnB5 steel. Furthermore, an actual warm-stamped B-pillar of medium-Mn steel is stamped and ultra-fine-grained martensitic microstructure is obtained. The mechanical properties are evenly distributed. As a result, this paper proves that the warm-stamped medium-Mn steel part can meet the requirements of lightweight and crash safety, and is promising for the industrial production of automotive structural parts.