Making polymer brush photosensitive with azobenzene containing surfactants

详细信息    查看全文

• 作者：Alexey Kopyshev^a ; Nino Lomadze^a ; David Feldmann^a ; Jan Genzer^b ; Svetlana Santer^a ; ^{santer@uni-potsdam.de" class="auth_mail" title="E-mail the corresponding author}
• 关键词：Azobenzene containing cationic surfactants ; Photosensitive polymer brushes ; Opto-mechanically induced scission of polymer chains
• 刊名：Polymer
• 出版年：2015
• 出版时间：19 November 2015
• 年：2015
• 卷：79
• 期：Complete
• 页码：65-72
• 全文大小：1783 K

文摘

We report on rendering polyelectrolyte brushes photosensitive by loading them with azobenzene-containing cationic surfactants. Planar poly(methacrylic acid) (PMAA) brushes are synthesized using the “grafting from” free-radical polymerization scheme followed by exposure to a solution of photosensitive surfactants consisting of positively-charged head groups and hydrophobic tails into which azobenzene moieties are inserted. In this study the length of the hydrophobic methylene spacer connecting the azobenzene and the charged head group ranges from 4 to 10 CH₂ groups. Under irradiation with UV light, the photo-isomerization of azobenzene integrated into a surfactant results in a change in size, geometry, dipole moment and free volume of the whole molecule. When the brush loaded with photosensitive surfactants is exposed to irradiation with UV interference patterns, the topography of the brush deforms following the distribution of the light intensity, exhibiting surface relief gratings (SRG). Since SRG formation is accompanied by a local rupturing of polymer chains in areas from which the polymer material is receding, most of the polymer material is removed from the surface during treatment with good solvent, leaving behind characteristic patterns of lines or dots. The azobenzene molecules still integrated within the polymer film can be removed by washing the brush with water. The remaining nano-structured brush can then be re-used for further functionalization. Although the opto-mechanically induced rupturing occurs for all surfactants, larger species do not penetrate deep enough into the brush such that after rupturing a leftover layer of polymer material remains on the substrate. This indicates that rupturing occurs predominantly in regions of high surfactant density.