Fabrication and ferroelectric/dielectric properties of La-doped PMN-PT ceramics with high optical transmittance
详细信息 查看全文
- 作者：Zhenzhen Song ; Yongcheng Zhang ; qdzhyc@163.com ; Chaojing Lu ; cjlu@qdu.edu.cn ; Zhenmeng Ma ; Zhenjia Hu ; Lin Wang ; Chao Liu
- 关键词：PMN-PT ; Transparent ceramics ; La doping ; Relaxor ferroelectric
- 刊名：Ceramics International
- 出版年：2017
- 出版时间：March 2017
- 年：2017
- 卷：43
- 期：4
- 页码：3720-3725
- 全文大小：1236 K
- 卷排序：43
文摘
Relaxor ferroelectric 0.75(Pb1–3x/2Lax)(Mg1/3Nb2/3)O3-0.25(Pb1–3x/2Lax)TiO3 (La3+:PMN-PT x/75/25, where x=2.8, 3.0, 3.5, and 4.0 mol% of La3+) transparent ceramics were fabricated by the combination of oxygen atmosphere pressureless sintering and hot-pressing sintering process. The optical transmittances of above four ceramics are higher than 60% at the wavelength of 500–900 nm. La3+:PMN-PT 3.0/75/25 exhibits the highest transparency around 70% at 900 nm which is very close to the theoretical transmittance 71%. Each of the four ceramics exhibits the pure perovskite phases. They show fully dense microstructures and their relative densities are higher than 99.8%. The ferroelectric and dielectric measurements indicate that these four ceramics exhibit relaxation characteristics. With increasing La3+ content, (200) peak in XRD patterns shifts to higher angles and the average grain size increases, while the temperature Tεmax corresponding to the maximum εr, the remanent polarizations Pr and coercive fields Ec decrease gradually.